弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 泊松比(Poissons Ratio):0.29 剪切模量(Shear Modulus):77.0 GPa(11200 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear): 17.3 μm/m-℃(@Temperature 0-100 ℃) 17.8 μm/m-℃(@Temperature 0-315 ℃) 18.4 μm/m-℃(@Temperature 0-...
剪切模量(Shear Modulus):77.0 GPa(11200 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear):17.3 μm/m-℃(@Temperature 0-100℃) 17.8 μm/m-℃(@Temperature 0-315℃) 18.7 μm/m-℃(@Temperature 0-650℃) 比热容(Specific Heat Capacity):0.500 J/g-℃(@Temperature 0-100℃) 热导率...
Modulus of elasticity 190-210 GPa Bulk modulus (Typical for steel) 140 GPa Shear modulus (Typical for steel) 80 GPa Poissons ratio 0.27-0.30 Elongation at break (in 50 mm) 21.50% Reduction of area 59.6 Hardness, Brinell 217 Hardness, Knoop (Converted from Brinell hardness) 240 Hardness, Roc...
Shear Modulus (Typical for steel) 80 GPa 11600 ksi Heat Treatment AISI 1045 is subjected to various heat treatment processes to optimize its mechanical properties: Forging - Heat to 850 °C - 1250°C (1562 °F – 2282 °F). Hold until the temperature is uniform. Cool in a furnace. Anne...
Compared to the Fe matrix, the elastic modulus (B), shear modulus (G), Young's modulus (E), and hardness (Hv) of Al2O3, LaAlO3, and CeAlO3differ significantly, while the corresponding values of CaAl2O4, Ca3Al2O6, and Ca12Al14O33are all lower than those of the Fe matrix ...
According to EC3, the modulus of elasticity of steel Es = 210 000 N/mm2, shear modulus G = 81,000 N/mm2, Poisson's ratio in elastic stage ν = 0.3, and the coefficient of linear thermal expansion α = 12 × 10− 6 per K (for T ≤ 100 °C). It should be noted that for ...
Shear modulus (typical for steel)80 GPa11600 ksi Elastic modulus190-210 GPa27557-30458 ksi Poisson’s ratio0.27-0.300.27-0.30 Elongation at break (in 50 mm)25.70%25.70% Hardness, Brinell197197 Hardness, Knoop (converted from Brinell hardness)219219 ...
Shear modulus (Typical for steel) 80 GPa 11600 ksi Poissons ratio 0.27-0.30 0.27-0.30 Elongation at break (in 50 mm) 21.50% 21.50% Reduction of area 59.6 59.60% Hardness, Brinell 217 217 Hardness, Knoop (Converted from Brinell hardness) 240 240 Hardness, Rockwell B (Converted from Brinell ...
Shear Modulus 77.0 GPa 11200 ksi Estimated from elastic modulus Electrical PropertiesMetricEnglishComments Electrical Resistivity 0.0000174 ohm-cm 0.0000174 ohm-cm Typical steel Thermal PropertiesMetricEnglishComments CTE, linear 11.3 µm/m-°C@Temperature 21.0 - 480...
抗拉强度(强度极限)(Tensile Strength, Ultimate):1115 MPa(125000 psi) 弹性模量(Tensile Modulus):193 GPa(28000 ksi) 188 GPa (@Temperature -195 ℃) 泊松比(Poissons Ratio):0.25 疲劳强度(Fatigue Strength ):485 - 550 MPa (70300 - 79800 psi) 剪切模量(Shear Modulus):77.2 GPa(11200 ksi) 热性能...