Shear modulus (typical for steel)80 GPa11600 ksi Poisson’s ratio0.27-0.300.27-0.30 Izod Impact115 J84.8 ft.lb Hardness, Brinell149149 Hardness, Knoop (converted from Brinell hardness)169169 Hardness, Rockwell B (converted from Brinell hardness)8080 ...
Shear modulus (Typical for steel) 80 GPa 11600 ksi Poissons ratio 0.27-0.30 0.27-0.30 Elongation at break (in 50 mm) 21.50% 21.50% Reduction of area 59.6 59.60% Hardness, Brinell 217 217 Hardness, Knoop (Converted from Brinell hardness) 240 240 Hardness, Rockwell B (Converted from Brinell ...
弹性模量(Tensile Modulus):193 GPa(28000 ksi) 188 GPa (@Temperature -195 ℃) 泊松比(Poissons Ratio):0.25 疲劳强度(Fatigue Strength ):485 - 550 MPa (70300 - 79800 psi) 剪切模量(Shear Modulus):77.2 GPa(11200 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear): 17.2 μm/m-℃(@Tempe...
弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 泊松比(Poissons Ratio):0.29 剪切模量(Shear Modulus):77.0 GPa(11200 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear): 17.3 μm/m-℃(@Temperature 0-100 ℃) 17.8 μm/m-℃(@Temperature 0-315 ℃) 18.4 μm/m-℃(@Temperature 0-...
1 psi (lb/in2 ) = 0.001 ksi = 144 psf (lb f /ft2 ) = 6,894.8 Pa (N/m2 ) = 6.895x10 -3 N/mm2 Related: Engineering Properties of Metals Yield Strength review and materials chart Modulus of Elasticity, Average Properties of Structural Materials, Shear Modulus, Poisson's Ratio,...
Bulk Modulus (Typical for steel) 140 GPa 20300 ksi Poissons Ratio (Typical For Steel) 0.290 0.290 Shear Modulus (Typical for steel) 80 GPa 11600 ksi Heat Treatment Looking for equipment to analyze your metals? Let us source quotes for you for X-Ray Fluorescence Analyzers, Optical Emission Spe...
Shear Modulus 11,500 ksi 79.3 GPaHow A36 is MadeA36 is made in a fashion similar to most carbon steels. First, iron ore and coal are combined in a furnace. Impurities are burned away and alloying elements are added to the molten steel. Once the chemical composition of the A36 steel is...
Shear modulus (typical for steel) 80 GPa 11600 ksi Elastic modulus 190-210 GPa 27557-30458 ksi Poisson’s ratio 0.27-0.30 0.27-0.30 Elongation at break (in 50 mm) 25.70% 25.70% Hardness, Brinell 197 197 Hardness, Knoop (converted from Brinell hardness) 219 219 Hardness, Rockwell B (conver...
Shear modulus (Typical for steel)80 GPa11600 ksi Poissons ratio0.27-0.300.27-0.30 Elongation at break (in 50 mm)21.50%21.50% Reduction of area59.659.60% Hardness, Brinell217217 Hardness, Knoop (Converted from Brinell hardness)240240 Hardness, Rockwell B (Converted from Brinell hardness)9595 ...
Shear modulus (typical for steel)80 GPa11600 ksi Poisson’s ratio0.27-0.300.27-0.30 Izod Impact115 J84.8 ft.lb Hardness, Brinell149149 Hardness, Knoop (converted from Brinell hardness)169169 Hardness, Rockwell B (converted from Brinell hardness)8080 ...