Tensile strength530 MPa76900 psi Yield strength385 MPa55800 psi Elastic modulus190-210 GPa27557-30458 ksi Bulk modulus (typical for steel)140 GPa20300 ksi Shear modulus (typical for steel)80 GPa11600 ksi Poisson’s ratio0.27-0.300.27-0.30 ...
屈服强度(屈服极限)(Tensile Strength, Yield):≥205 MPa(29700 psi)(@Strain 0.2%) 断裂延伸率(Elongation at Break):≥40% 断面收缩率(Reduction of Area):≥50% 弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 泊松比(Poissons Ratio):0.29 剪切模量(Shear Modulus):77.0 GPa(11200 ksi) 热性能(Th...
弹性模量(Tensile Modulus):193 GPa(28000 ksi) 188 GPa (@Temperature -195 ℃) 泊松比(Poissons Ratio):0.25 疲劳强度(Fatigue Strength ):485 - 550 MPa (70300 - 79800 psi) 剪切模量(Shear Modulus):77.2 GPa(11200 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear): 17.2 μm/m-℃(@Tempe...
Tensile strength, yield460 MPa66700 psi Modulus of elasticity190-210 GPa27557-30458 ksi Bulk modulus (Typical for steel)140 GPa20300 ksi Shear modulus (Typical for steel)80 GPa11600 ksi Poissons ratio0.27-0.300.27-0.30 Elongation at break (in 50 mm)21.50%21.50% ...
Shear Modulus (Typical for steel) 80 GPa 11600 ksi Heat Treatment Looking for equipment to analyze your metals? Let us source quotes for you for X-Ray Fluorescence Analyzers, Optical Emission Spectrometers, Atomic Absorption Spectrometers or any other analysis instrument you are looking for. Request...
Yield strength415 MPa60200 psi Bulk modulus (typical for steel)140 GPa20300 ksi Shear modulus (typical for steel)80 GPa11600 ksi Elastic modulus190-210 GPa27557-30458 ksi Poisson’s ratio0.27-0.300.27-0.30 Elongation at break (in 50 mm)25.70%25.70% ...
Shear Modulus80.0GPa11600ksiTypical for steel Izod Impact110J81.1ft-lb Electrical PropertiesMetricEnglishComments Electrical Resistivity0.0000159ohm-cm @Temperature 0.000 °C0.0000159ohm-cm @Temperature 32.0 °Fannealed condition 0.0000219ohm-cm @Temperature 100 °C0.0000219ohm-cm ...
Shear Modulus80.0GPa11600ksiTypical for steel Electrical PropertiesMetricEnglishComments Electrical Resistivity0.0000159ohm-cm @Temperature 0.000 °C0.0000159ohm-cm @Temperature 32.0 °Festimated by comparison with similar materials Thermal PropertiesMetricEnglishComments ...
Ultimate Strength Yield Point X 1000/in2 Modulus of Elasticity (T) Tension X 1000/in2 Compression, in terms of T Shear in terms of T in Tension (E) x 106 psi in Shear, in terms of E Cast iron, grey, class 20 20a 3.6 T - 4.4 T 1.6 T ... 11.6 0.40 E class 25 25a 3.6...
Poisson's Ratio0.2650.2750.2650.275NULL Shear Modulus7481GPa10.732811.7481106psi Tensile Strength510620MPa73.969289.9234ksi Young's Modulus190203GPa27.557229.4426106psi Glass TemperatureK°F Latent Heat of Fusion260285kJ/kg111.779122.527BTU/lb