the enlarged view (in Fig.3c) [42,43]. The 1 T phase presence in Raman spectra corresponds to the forward shifted (002) peak of MoS2in XRD, which is due to the NaBH4providing Na⁺ for intercalation and a significant amount of electron reducibility during the preparation process [44]. ...
The successful interface between TiO2 and rGO was confirmed by the broadening characteristic of the XRD peak for anatase TiO2, increasing D and G band intensity ratios (ID/IG) of Raman spectra from 1.05 to 1.9, and decreasing intensity of UV–Vis transmittance spectra as the rGO concentration ...
impurities peaks, which confirms the successful formation of a ternary nanocomposite. Moreover, the implementation of GCN and rGO in the SRT sample varies/decreases the XRD peak intensities which may be due to the influence of GCN and rGO sheets being successfully deposited on the SRT sample. Th...
Although the C1s spectrum is mixed with RGO and CNT, the highest intensity in the C-C/C=C peak at 284.4 eV suggests the reduction of oxygen functional groups within RGO and the effective restoration of sp2 carbon network34. In situ XRD and de-intercalation. i n situ XANE The...
The enhanced characteristic peak of 1382 cm−1 in BWO-a/rGO compared with BWO and BWO-a may be due to the interface connection between rGO and BWO-a [54]. Notably, the characteristic absorption peak intensity of BWO-a and BWO-a/rGO are significantly more substantial than that of BWO...
The XRD results of PdNi revealed that there was no significant nickel diffraction peak, due to the fact that synthesized nanoparticle has stronger signals for the palladium, which is associated with the amorphous structure. Using the Eq. 1, the average size of crystal particles was calculated ...
(area) and intensity mainly arises from overlapping of D1 and D4 peaks in the band region of 1100–1400 cm−1, suggesting that the Scientific Reports | 5:16195 | DOI: 10.1038/srep16195 3 www.nature.com/scientificreports/ Figure 2. XRD pattern of: (a) M30, M60, and M90 on...
An XRD pattern of CNS@rGO after stability testing further confirms the structural stability of the bi-metal nanoarrays, as shown in Fig. S12. As a result, the particular structural advantages (vertically grown nanoarrays) has benefit for improving the stability, although metal-support electronic ...
While the XRD spectrum for rGO-nZVI NH before PFAS removal test (Fig. S6a) shows only a sharp peak for Fe°, the XRD spectra for rGO-nZVI NH after PFAS removal tests show peaks for Fe2O3 and β-FeOOH (lepidocrocite) (Vernekar and Jagadeesan, 2015; Wang et al., 2015) in the ...
X-ray diffraction (XRD), Raman spectroscopy, and field emission scanning electron microscopy (FE-SEM) were used to analyze the crystalline structure, material composition, and surface appearance characteristics of the sensing material. By combining the material with a commercial near-field communication...