Tensile strength, yield (@20°C/68°F, varies with heat treatment) 1000 – 1380 MPa 145000 – 200000 psi Reduction of area (@20°C/68°F) 50.00% 50.00% Modulus of elasticity (@20°C/68°F) 215 GPa 31200 ksi Poisson’s ratio 0.27-0.30 0.27-0.30 5. Forging of H13 Tool Steel Hea...
H13 Tool Steel is a high hot-wear resistance and great strength, warm conductivity and invulnerability to hot cracking.
AISI H13 Steel Properties High hot-wear resistance and hot tensile strength as well as good toughness, thermal conductivity and insusceptibility to hotcracking. Can be water-cooled to a limited extent. Mechanical Properties: Tensile strength 1550 MPa-2050MPa Yield Strength 1000-1380 MPa Elongation...
H13 Ibol Steel printed on the Metal X washed in the and sintered in the Sinter-1. As Sintered Microstructure is pictured to the left • Markforged H13 Heat Ideated H13 Idol Steel printed Wi the Metal X system, air quenched at 1010C ...
AISI H13 tool steeldeep cryogenic treatmentmechanical propertiesIn this study, a number of wear and tensile tests were performed to elucidate the effects of deep cryogenic treatment on the wear behavior and mechanical properties (hardness and tensile strength) of AISI H13 tool steel. In accordance ...
The LC H13 tool steel showed excellent tensile properties (Table 17.2). The average yield and tensile strengths of the as-consolidated H13 along vertical direction were about 1288 MPa and 2064 MPa respectively, while the elongation was about 6% and the elastic modulus (E) was about 216 GPa....
H13 tool steel is a high-carbon, high-chromium hot work tool steel widely used in various industrial applications due to its exceptional properties, including high wear resistance, dimensional stability, and hot hardness. To ensure the consistent quality and performance of H13 tool steel, several ...
MATERIAL DATASHEET H13 Tool Steel Composition Chromium Molybdenum Silicon Vanadium Carbon Manganese Phosphorous Sulfur Iron Amount 4.7-5.5% 1.3-1.7% 0.8-1.2% 0.8-1.2% 0.3-0.45% 0.2-0.5% 0.03% max 0.03% max bal 50um 1800 1600 1400 1200 1000 800 600 400 200 0 0 H13 Markforged Heat Treated...
The mechanical properties of H13 tool steels are tabulated below. PropertiesMetricImperial Tensile strength, ultimate (@20°C/68°F, varies with heat treatment)1200 - 1590 MPa174000 - 231000 psi Tensile strength, yield (@20°C/68°F, varies with heat treatment)1000 - 1380 MPa145000 - 200000...
4: AISI H13 Steel Mechanical Properties The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized,...