Excellent through-hardening properties Very limited distortion during hardening In steel H13, the molybdenum and vanadium act as strengthening agents. The chromium content assists die steel H-13 to resist softening when used at high temperatures. H-13 die steels offers an excellent combination of sho...
H13 tool steel contains a composition of approximately 1.4% to 1.6% carbon, 4.75% to 5.5% chromium, 0.3% to 1% molybdenum, 1% vanadium, and smaller amounts of other alloying elements such as silicon and manganese. This specific composition contributes to its excellent properties, including high...
H13 Tool Steel: Standards and Requirements. H13 tool steel is a high-carbon, high-chromium hot work tool steel widely used in various industrial applications due to its exceptional properties, including high wear resistance, dimensional stability, and hot hardness. To ensure the consistent quality ...
H13 tool steel contains a composition of approximately 1.4% to 1.6% carbon, 4.75% to 5.5% chromium, 0.3% to 1% molybdenum, 1% vanadium, and smaller amounts of other alloying elements such as silicon and manganese. This specific composition contributes to its excellent properties, including high...
What is the Hardness of H13 Tool Steel? Hardness tests determine the various properties of a specific metal, which includes its resistance to wear, toughness, and formability. Two widely used tests are Rockwell C and Brinell. Rockwell C is measured in the unit HRC, which is the measurement ...
H13 Idol Steel printed Wi the Metal X system, air quenched at 1010C and double tempered at 600C • Wrought H13 Heat Treated Wrought H13 too! steel standard from ASM Spedafty Handbook-air quenched at 1010C and double tempered at 600C.Typical Mechanical Properties Standard Markforged As-Sinter...
WU Cui-lan,LUO Cheng-ping,ZOU Gan-feng.Microstructure and properties of low-temperature composite chromized layer on H13 tool steel. Journal ofMaterial and Technology . 2005WU Cui-lan,LUO Cheng-ping,ZOU Gan-feng.Microstructure and properties of low-temperature composite chromized layer on H13 ...
AISI H13 tool steel is characterized by: High level of toughness and ductility Good resistance to abrasion at both low and high temperatures Good high-temperature strength High through-hardening properties Very limited distortion during hardening ...
The physical properties of H13 tool steels are given in the following table. PropertiesMetricImperial Density (@20°C/68°F)7.80 g/cm30.282 lb/in3 Melting point1427°C2600°F Mechanical Properties The mechanical properties of H13 tool steels are tabulated below. ...
andgas nitriding. To improve the surface properties, H13 tool steel are quite often gas nitrided. In recent studies, microscopic examinations have shown the presence of compound layer in the outer surface. This is a white layer of thickness 5µm. Microanalysis shows that the layer has higher...