the most signif i cant difference between E8 and E8M testspecimens. Test specimens made from powder metallurgy(P/M) materials are exempt from this requirement by industry-wide agreement to keep the pressing of the material to aspecif i c projected area and density.1.3 Exceptions to the ...
ASTM E8/E8M-21金属材料拉伸试验方法Standard Test Methods for Tension Testing of Metallic Materials 1
33 p. ASTM_E8M-2004 17 p. ASTM_A513-07 17 p. ASTM_A513-06a电阻焊碳素钢与合金钢机械钢管 39 p. ASTM D2000(中文版) 4 p. ASTM D1364-02(2012) Standard Test Method for Water in Volatile Solvents (Karl Fischer Reagent Titration Method) 3 p. ASTM D1177-07(英文) 发动机冷却水...
内容提示: Designation: E8/E8M − 22 American Association StateHighway and Transportation Officials StandardAASHTO No.: T68An American National StandardStandard Test Methods forTension Testing of Metallic Materials 1This standard is issued under the f i xed designation E8/E8M; the number immediately...
1.2 大多数圆形试样的标距长度要求为 E8 为 4D,E8M 为 5D。标距长度是 E8 和 E8M 测试样本之间最显着的差异。根据行业协议,由粉末冶金 (P/M) 材料制成的测试样本可免除此要求,以将材料压制到特定的投影面积和密度。1.3 对于特定材料,可能需要在单独的规范或测试方法中对这些测试方法的规定进行例外规定。例如...
金属材料拉伸试验-美标ASTM E8/E8M 金属材料拉伸试验方法 公司名称:广州市安普检测技术服务有限公司www.gzaptest.com 金属材料抵抗外力引起变形和断裂的能力称之为金属材料的力学性能,抗拉力则是力学性能中最重要的性能之一。拉伸试验是标准拉伸试样在静态或动态轴向拉伸力不断作用下以规定的拉伸速度拉至试样断裂并在...
|ASTM E8M用于金属材料拉伸试验的标准试验方法 ASTM E8/E8M描述了环境温度下的金属单轴拉伸试验,以及规定塑性延伸强度、屈服强度、屈服点伸长、拉伸强度、断裂应变和断面收缩等特性值的测定。 这些值可用于预测材料的强度和韧性。 ASTM E8和ASTM E8M的区别 ...
1.1本试验方法涵盖了任何形式的金属材料在室温下的拉伸试验,具体包括屈服强度、屈服点伸长率、抗拉强度、伸长率和断面收缩率的测定方法。 1.2 大多数圆形试样的标距长度要求为 E8 为 4D,E8M 为 5D。标距是 E8 和 E8M 试样之间最显着的差异。根据行业范围内达成的协议,由
1.1 本试验方法涵盖了任何形式的金属材料在室温下的拉伸试验,具体包括屈服强度、屈服点伸长率、抗拉强度、伸长率和断面收缩率的测定方法。 1.2 大多数圆形试样的标距长度要求为 E8 为 4D,E8M 为 5D。标距是 E8 和 E8M 试样之间最显着的差异。根据行业协议,由粉末冶金 (P/