1.1 这些试验方法涵盖室温下任何形式的金属材料的拉伸试验,具体而言,包括测定屈服强度、屈服点伸长率、抗拉强度、伸长率和断面收缩率的方法。1.2 大多数圆形试样的标距长度要求为 E8 的 4D 和 E8M 的 5D。标距长度是 E8 和 E8M 试样之间最显著的差异。根据行业协议,由粉末冶金 (P/M) 材料制成的试样不受此要求限
Designation: E8/E8M − 24 American Association StateHighway and Transportation Officials StandardAASHTO No.: T68An American National StandardStandard Test Methods forTension Testing of Metallic Materials 1This standard is issued under the f i xed designation E8/E8M; the number immediately following...
1.1 本方法适用于室温下任何形状的金属材料的拉伸试验。特别是对于屈服强度、屈服点延伸率、抗拉强度、延伸率和断面收缩率的测定。 1.2 E8和E8M试样最大的区别在于原始标距,E8中对于大多数圆形试样标距长度的要求是4D,而E8M是5D,实际生产中一般认为用粉末冶金(PM)材料制成的试样可无此要求,以保持工业要求的材料...
未注明发布机构,关于astm e8-24的标准ASTM E659-24 ASTM E659-24本站其他标准专题: astm +/for,astm +a276/+ astm,astm a325 astm,astm +a325+ astm,astm +6278+ astm,astm astm+3588,astm astm+2709,astm269 astm,astm d astm d 6198,astm ieee/astm si 10,astm astm b108,astm astm+d6377,astm...
Referenced Documents2.1 ASTM Standards: 2E4 Practices for Force Calibration and Verif i cation of Test-ing MachinesE8/E8M Test Methods for Tension Testing of Metallic Ma-terialsE21 Test Methods for Elevated Temperature Tension Tests ofMetallic MaterialsE23 Test Methods for Notched Bar Impact Testing...
31、 ASTM E8/E8M-24 Standard Test Methods for Tension Testing of Metallic Materials 32、 ASTM E3369-24 Standard Specification for Determining the Flood Damage Resistance Rating of Building Materials 33、 ASTM F2562/F2562M-24 Specification for Steel Reinforced Thermoplastic Ribbed Pipe and Fittings ...
A518M ASTM A532/A532M ASTM A536 ASTM A571/A571M ASTM A644 ASTM A802/A802M ASTM A823 ASTM A842 ASTM A874/A874M ASTM A897/A897M ASTM A941 ASTM E10 ASTM E1019 ASTM E165/E165M ASTM E1806 ASTM E29 ASTM E351 ASTM E689 ASTM E709 ASTM E8/E8M ASTM E802 ASTM E94/E94M MIL-ST...
ASTM F384-24 引用标准 ASTM E122 ASTM E4 ASTM E8/E8M ASTM F136 ASTM F138 ASTM F2503 ASTM F382 ASTM F565 ASTM F620 ASTM F621 ASTM F983 ISO 14602 ISO 5835 ISO 5836 ISO 9268 ISO 9269 购买 正式版1.1 这些规范和测试方法为用于骨骼系统外科内固定的成角度装置提供了全面的参考。本标准建立了...
Sf,舶darddoesnorpurporttoαdd陀的allofthesα1fetyconcerns,E8/E8MTestMethodsforTensionTestingofMetallicMa- terials (fa町,削sociatedwithitsuse.Itisth们espo时ibil峙。ifti,随时er ofthisstand,αrdrobecomefamiliarwithallhazardsincludingEl8TestMethodsforRockwellHardnessofMetallicMa- ...
成分,物理性能及机械性能—本烧结料采用标准试棒测定时,其性能应符合表1和表2的要求(见E8检测方法)。 显微组织—每个样品经放大200倍检查,其显微组织应显示钨粒子在金属粘合剂的基体中分布均匀。可以规定检验部位(见8.4.5)。 机加工性能—如有规定(见),基本部件或相应试样的机加工性能应能经受8.4.6规定的试验。