glass platesradial cracksresidual stressesThe fracture patterns which develop during the ballistic impact of two series of three layer glass/polycarbonate/glass impact resistant glass panels laminates were studied for both annealed glass and heat strengthened glass plates in the glass panels. The cracking...
The fracture patterns which develop during the ballistic impact of two series of three layer glass/polycarbonate/glass impact resistant glass panels laminates were studied for both annealed glass and heat strengthened glass plates in the glass panels. The cracking patterns are qualitatively described. ...
These were cut from a single annealed glass plate, and identically processed on a single cutting and grinding line. One third of these were tested in the annealed condition, one third heat strengthened and one third was fully tempered. All specimens were tested in four point bending. Weibull ...
The strength of annealed, heat-strengthened and fully tempered float glass. F. A. VEER,P. C. LOUTER,F. P. BOS. Fatigue and Fracture of Engineering Materials and Structures . 2009F. A. Veer, F. P. Bos, and P. C. Louter, "The strength of annealed, heat strengthened and fully ...
“Standard Test Method for Non-Destructive Photoelastic Measurement of Edge and Surface Stresses in Annealed,Heat-Strengthened and Fully Tempered Flat Glass,”.ASTM C1279. 2000ASTM C1279, "Standard Test Method for Non-Destructive Photoelastic Measurement of Edge and Surface Stresses in Annealed, Heat...