抗拉强度(强度极限)(Tensile Strength, Ultimate):≥515 MPa(74700 psi) 屈服强度(屈服极限)(Tensile Strength, Yield):≥205 MPa(29700 psi)(@Strain 0.2%) 断裂延伸率(Elongation at Break):≥40% 断面收缩率(Reduction of Area):≥50% 弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 泊松比(Poissons...
屈服强度(屈服极限)(Tensile Strength, Yield):215 MPa(31200 psi) 断裂延伸率(Elongation at Break):70% 弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 泊松比(Poissons Ratio):0.29 剪切模量(Shear Modulus):77.0 GPa(11200 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear):17.3 μm/m-℃...
The yield strength of 304 stainless steel is 205 MPa (29,700 psi). Yield strength represents the maximum stress a material can endure while maintaining elastic deformation. This value may vary depending on factors such as heat treatment and specific manufacturing processes. What is the Tensi...
Nickel8.50 to 10.50% max. Mechanical Properties Tensile strength100,000 to 180,000 psi Yield strength50,000 to 150,000 psi Elongation in Two Inches55 to 60% Reduction in Area55 to 65% Modulus of Elasticity29,000,000 psi Density.286 lbs/cubic inch ...
Ultimate Tensile Strength73,200psi310 MPa Yield Tensile Strength31,200psi276 MPa Melting Point2,550 - 2,651°F1,400 - 1,455°C TemperAnnealed Hardness RockwellB70 Hardness Brinell123 The provided chemical compositions and mechanical properties are general approximations. Please contact our Customer Se...
Ultimate Tensile Strength73,200psi310 MPa Yield Tensile Strength31,200psi276 MPa Melting Point2,550 - 2,651°F1,400 - 1,455°C TemperAnnealed Hardness RockwellB70 Hardness Brinell123 The provided chemical compositions and mechanical properties are general approximations. Please contact our Customer Se...
GradeTensile Strength ksi (min)Yield Strength 0.2% ksi (min)Elongation %Hardness (Brinell) MAXHardness (Rockwell B) MAX 304L 70 25 40 201 92 Physical Properties: Density lbm/in3Thermal Conductivity (BTU/h ft. °F)Electrical Resistivity (in x 10-6)Modulus of Elasticity (psi x 106Coefficien...
TENSILE PROPERTY REQUIREMENTS TENSILE STRENGTH, MIN YIELD STRENGTH, MIN ELONGATION IN 2” or 50 mm HARDNESS, MAX TYPE psi MPa psi MPa MIN, % BRINELL ROCKWELL B 304 75,000 515 30,000 20 40 200 92Products Stainless Steel Banding Color Fast™ Cut to Length Band Band Tools Buckles Sign ...
Tensile Strength: 75 ksi Yield Point: 30 ksi Elasticity: 28 ksi Elongation in 2": 60% Brinell Hardness: 160 Melting Point: 2550F Density: 0.289 lb/in3 Yield Tensile Strength: 31,200 psi Poisson Ratio: 0.29 Company Profile Bozhong Group Mainly...
Tensile Yield Strength 60200 psi 31200 psi Hardness (Rockwell B) 96 96 Elongation at Break 40% 70% 303 vs. 304 stainless steel appearance 303 and 304 have similar appearances and are often visually indistinguishable. Both alloys have a face-centered cubic crystal structure and a similar surfa...