On the other hand, the magnetoresistance is found to show positive and negative ones. The resistivity and the corresponding positive magnetoresistance become larger as the growth temperature of crystal becomes higher and/or as the doping amount of Se becomes more. Below about 0.1 K, only the ...
in the Anderson Localized State]]>The electrical resistivity and magnetoresistance of 1T-TaS2−xSex (x=0–0.4) have been measured from a few Kelvin ... Akio,Furukawa,Yasukage,... - 《Journal of the Physical Society of Japan》 被引量: 0发表: 1984年 Anisotropically electrical property of...
Anomalous magnetoresistance in 1T-TaS2doi:10.1016/0375-9601(78)90078-6Transverse magnetoresistance of 1T-TaS2 was measured in magnetic fields up to 100 kOe in the semiconductive region corresponding to the commensurate charge density wave (CDW) state.S....
The magnetoresistance of 1 T-TaS 2 in the commensurate CDW phase was measured from 8 K down to 50 mK. Very large negative magnetoresistance was observed below 0.5 K for both transverse and longitudinal configurations of the magnetic field with respect to the current. This result is explained ...
The temperature dependences of the Seebeck effect and transverse magnetoresistance are systematically observed on 1T-TaS2 with various qualities. The Seebeck coefficient is positive in commensurate CDW state and its temperature dependence in 20 K ⪅ T ⪅ 60 K seems to indicate that the samples ...
magnetoresistancetantalum compoundstitanium compoundsZeeman effect/ magnetoresistancescaling theoryTaS 21T polytypeZeeman effecttwo-dimensional Anderson localisationAnalysis of magnetoresistance of 1T-TaS 2 and its alloys is made based on the recent scaling theory of Anderson localization in two dimensions....
magnetoresistanceAnderson localisationThe temperature dependence of electrical resistivities θ( T) of 1T-TaS 2, 1T-TaS 2- xSe x and 1T-Fe xTa 1- xS 2 is found to be θ( T) ∝ exp( T 0/ T) 1/n in the temperature range of 4 K to the measured lowest temperature, 0.1 K, ...