Willemite (Zn 2 SiO 4 :Mn) is doped with one or more ions selected from the group formed by Gd 3+ , Eu 2+ , Co 2+ , Ce 3+ , Pr 3+ , Nd 3+ , Sm 3+ , Tb 3+ , Dy 3+ , Ho 3+ , Er 3+ , Tm 3+ and Yb 3+ . This results in a increase in absorption and ...
三、本文首次采用燃烧法,制备得到了Zn2SiO4:Eu3+红色荧光粉,其最佳制备条件是:在600℃燃烧、1100℃保温、保温时间为2小时。并用XRD、SEM、UV-Vis、荧光等对Zn... 彭子飞[1],余军保[1],徐捷[1],... - 《上海师范大学》 被引量: 5发表: 2007年 ...
溶胶-凝胶法制备Zn2SiO4：Eu 3+红色荧光粉
燃烧法制备Zn2SiO4：Eu 3+红色荧光粉及其发光性能 维普资讯 http://www.cqvip.com
Spherical SiO 2 particles have been coated with Zn 2SiO 4:Eu 3+ phosphor layers by a Pechini sol–gel process. The microstructure and luminescent properties of the obtained Zn 2SiO 4:Eu 3+@SiO 2 particles were well characterized by X-ray diffraction (XRD), Fourier transform infrared spectro...
Luminescent composites of poly(methylmethacrylate) (PMMA) and nanophosphors (Zn 2 SiO 4 :Mn 2+ , Zn 2 SiO 4 :Eu 3+ ) were prepared by dispersion casting method. It was found that nanoparticles embedded in PMMA matrix preserve their typical phosphorescence emission. The influence of Zn 2 ...
激发谱(硅氧)的ca8zn 4cl2:Eu2 +的显示在激烈的激发带集中在450 nm处的蓝色,并用505 nm的最大发射。 翻译结果2复制译文编辑译文朗读译文返回顶部 Ca8Zn(SiO4) 4Cl2 的兴奋范围: Eu2 + 显示在蓝色中的一个强烈的兴奋波段在 450 nm 处居中和发表以一个最大值在 505 nm。 翻译结果3复制译文编辑译文朗...
Zn2SiO4 螢光體其平均粒徑約為200nm較利用固態反應法的100μm為小.光譜分析方面,Zn2SiO4:Eu3+螢光體呈現紅色特性光,最強吸收特性峰值為535nm,以535nm波長激發產生5D0→7F0,5D0→7F1,5D0→7F2,5D0→7F3,5D0→7F4 ,5D0→7F5等躍遷的放射峰,以5D0→7F2為最強的放射峰,波長為610nm;而Zn2SiO4:Tb...
本发明公开了一种红色荧光粉Zn2SiO4:Eu3+的制备方法,采用一种新的制备方法--燃烧法,以尿素为燃烧剂,成功合成了Zn2SiO4:Eu3+红色荧光粉.通过加入少量的燃烧助剂硝酸铵,提高了燃烧放热量,产生过量的燃烧气体,使燃烧产物更加疏松.燃烧助剂在混合物内部点燃还可催化整个燃烧反应,有助于体系克服高的反应活化能势垒....
采用燃烧法合成了发光性能良好的Zn2SiO4:Eu3+红色荧 光体. 结果表明:经过600 ℃燃烧的样品在1000 ℃下煅烧可得到纯Zn2SiO4晶相. 利用XRD, SEM对样品的结构以及形貌进行表征,还考察了煅烧温度对Zn2SiO4:Eu3+荧光体发射强度及色度的影响,样品发射光谱为Eu3+的特征发射; 增大煅烧温度,发射强度增大,色度降低. ...