Sliding tests were conducted, in air, of YTZP ceramic pins against steel discs at an applied pressure of 15.5 MPa over a speed range of 0.3 to 4.0 ms −1 . Pin wear was not detectable until 2.0 m s −1 , after which a finite but small wear rate was observed at 3.0 m s −...
Wear Resistant YTZP Ceramic / ZrO2 / Zirconia Rod Zirconia ceramic due to its high toughness, high bending strength and thermal expansion coefficient close to the iron and steel, etc., it is widely used in elect-ronics, machinery, aerospace, petrochemical and other fields. As a...
ICS11.040.40 C35 中华人民共和国医药行业标准 / — YYT1715 2020 外科植入物 氧化钇稳定四方氧化锆 ( )陶瓷材料 Y-TZP — Im lantsforsurer Ceramicmaterialsbasedon ttria-stabilizedtetraonal p g y y g ( ) zirconiaY-TZP ( : , ) ISO133562015MOD 2020-06-30发布 2021-06-01实施 国家药品监督管理...
Other Alumina ceramic grinding ball introduction :This product are featured by high density and hardness, low wear lost, corrosion-resistance etc. They are the perfect high-efficient grinding media for milling glaze/frit, pigment, ceramic materials, and variou...
Ceramic films, containing AI2O3, with up to 40 vol% ZrO2, have been fabricated using the tape casting process. Finer powders (average mean diameter of 250... KP Plucknett,CH Cáceres,DS Willinson - 《Journal of the American Ceramic Society》 被引量: 140发表: 1994年 Grain Growth in Tw...
This technique has been used to join pieces of the same grain size and pieces with different grain sizes to produce a functionally gradient multilayered ceramic composite. Results concerning joining of Y-TZP will be also presented in this paper.A. Dominguez-Rodriguez...
In this work, a new lamination technique was employed to obtain laminated ceramic structures in the alumina-zirconia system with residual stress compression at the outer layers. This reinforcement mechanism would lead to ceramics with changed material properties and R-curve be...
Journal of the American Ceramic SocietyC. J. Szepesi and J. H. Adair, "High Yield Hydrothermal Synthesis of Nano-Scale Zirconia and YTZP," J. Am. Ceram. Soc., (in press).Szepesi CJ, Adair JH. High Yield Hydrothermal Synthesis of Nano-Scale Zirconia and YTZP. J Am Ceram Soc 2011;...
Acid-Basic Stability of Y-TZP Ceramics**Paper presented at the Symposium on Ceramic Materials Research at the E-MRS Spring Meeting, Strasbourg, May 31-June 2, 1988.J.C. FARIÑASR. MORENOJ. REQUENAJ.S. MOYA
The analysis of sintering curves revealed that a densification process takes place in the temperature range 800–1300°C with a well-defined maximum around 1100°C, leading to the formation of ceramic materials with fine equal grains. The dense sintered pellets obtained were used to study the ...