线材;5<d≤10 固溶+冷拔+固溶+调质轧制(+AT+C+AT+LC) ≤680 ≥63 棒材,杆材,线材;10<d≤25 固溶(+AT)或固溶+去皮 (+AT+PE) ≤630 ≥65 杆材,线材;10<d≤25 固溶+冷拔(+AT+C) ≤760 - 杆材, 线材;10<d≤25 固溶+冷拔+固溶(+AT+C+AT) ≤630 ≥68 棒材,杆材, 线材;25<d≤50 固...
X2CrNi18-9 1.4307 +AT 1000 to 1100 a,w -a-air w-water 物理性能 各温度°C时静态弹性模量 20°C与各温度间热膨胀系数 热导率 比热容 电阻率 20 100 200 300 400 500 600 700 800 100°C 200°C 300°C 400°C 500°C 600°C 20°C 20°C 20°C GPa 10-6 K-1 W/m.K J/kg.K ...
Brinell hardness (HB): (+A)215 Brinell hardness (HB): (+AT)200Properties of steel X2CrNi18-9 (1.4307) Resistance to intergranular corrosion: in the delivery condition - yes; in the sensitized condition - yesSteel shal not be applied at a metal temperature lower than -196 ° C本文禁止转...
④ The lower end of the range specified for solution annealing should be aimed at for heat treatment as part of further processing,because otherwise the mechanical properties might be affected. If the temperature of hot forming does not drop below the lower temperature for solution annealing.a ...
23、ope and at the international level. It is incorporated by Royal Charter.RevisionsBritish Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions.It is the constant aim of BSI to improve the quality of our...
布氏硬度(HB):(+A)215布氏硬度(HB):(+AT)200 钢X2CrNi18-9 (1.4307) 的性能 抗晶间腐蚀:在交货状态下 - 是;在敏化条件下 - 是 钢不得在低于 -196 °C 的金属温度下使用 应用 平底锅 弹簧、螺钉、螺母和螺栓 水槽和防溅板 建筑镶板 管道 ...
Brinell hardness (HB): (+A)215Brinell hardness (HB): (+AT)200 Properties of steel X2CrNi18-9 (1.4307) Resistance to intergranular corrosion: in the delivery condition - yes; in the sensitized condition - yes Steel shal not be applied at a metal temperature lower than -196 ° C...
X2CrNi18-9 1.4307 +AT 1000 to 1100 a,w - a-air w-water 物理性能 各温度°C时静态弹性模量 20°C与各温度间热膨胀系数 热导率 比热容 电阻率 20 100 200 300 400 500 600 700 800 100°C 200°C 300°C 400°C 500°C 600°C 20°C 20°C 20°C GPa 10-6 K-1 W/m.K J/kg.K...
Brinell hardness (HB): (+A)215 Brinell hardness (HB): (+AT)200Properties of steel X2CrNi18-9 (1.4307) Resistance to intergranular corrosion: in the delivery condition - yes; in the sensitized condition - yesSteel shal not be applied at a metal temperature lower than -196 ° C本文...
X2CrNi18-9 1.4307 +AT 1000 to 1100 a,w - a-air w-water 物理性能 各温度°C时静态弹性模量 20°C与各温度间热膨胀系数 热导率 比热容 电阻率 20 100 200 300 400 500 600 700 800 100°C 200°C 300°C 400°C 500°C 600°C 20°C 20°C 20°C GPa 10-6 K-1 W/m.K J/kg.K...