Superelasticity associated with the martensitic transformation has found a broad range of engineering applications1,2. However, the intrinsic hysteresis3 and temperature sensitivity4 of the first-order phase transformation significantly hinder the usage
NiCoFeGa single crystals exhibit large non-hysteretic superelasticity over broad temperature and composition ranges. It is attributed to the continuous phase transition with applied stress, which is related to the fluctuation of entangled ordered and disordered crystal structures....