The PCB sample measured exhibits a glass transition at 92 °C. This can be seen as a change in slope in the curve in Figure 1. The sudden dimensional change the z-direction at temperatures above 320 °C indicates that the sample begins to delaminate. This process was followed simultaneously...
In the OOT curve, the onset temperature of the oxidation (OOT) is determined as the extrapolated onset temperature. Figure 2 displays the results of the OOT measurements of DHA50-SA as a func- tion of the oxygen pressure. The linear relationship shows that the oxidation phenomenon is ...
Characteristic curve were calculated according to mortality risk estimated using Cox models adjusted for above mentioned traditional risk factors with versus without TMAO as previously described 19. All analyses performed used R 2.15.1 (Vienna, Austria). P<0.05 was considered statistically significant. R...
The PCB sample measured exhibits a glass transition at 92 °C. This can be seen as a change in slope in the curve in Figure 1. The sudden dimensional change the z-direction at temperatures above 320 °C indicates that the sample begins to delaminate. This process was followed simultaneously...