Ofl – x010 商业性的涂漆,只有与大众汽车股份公司中心实验室和/或奥迪 股份公司实验室及其主管设计部门商妥之后方可进行.对防腐蚀没有技术要求 Ofl –x100, Ofl –x300 Ofl –x600 预处理未作规定(但不能离开生产技术基础)单层 – 湿法涂漆方法不限,有选择地进行阴极浸渍涂漆(KTL) Ofl –x130 Ofl –x330 ...
The following changes have been made to TL 260: 2015-03:–Alternative pretreatment modified for Ofl-x330 –Chassis parts added for Ofl-x634 –Section 3.7 "Adhesion and brittleness" revised –Table 3, consec. no. 1.2: Requirements for corrosion resistance (corrosion cycle test as per PV ...
Ofl-x100,Ofl-x300, Olf-x600 预处理(非强制性规定),单层油漆和阴极电泳漆二者任选 Ofl-x130, Olf-x330 磷酸锌或磷酸铁/锰,单层油漆和阴极电泳漆二者任选 Ofl-x630 磷酸锌, 阴极电泳漆 Ofl-x631 磷酸锌,双层油漆(浸漆和喷漆) Ofl-x634 磷酸锌,厚层阴极电泳漆或双层浸漆(用于压力高的零件,例;前后...
Ofl-x330替代性预处理(基于氧化锆),磷酸锌、铁磷酸盐 处理或锰磷酸盐处理或三价磷酸盐处理; 单层-湿法涂漆方法不限,有选择地进行阴极浸渍 涂漆(KTL)(例如传动轴) Ofl-x630磷化锌或三价磷酸盐,KTL; 与大众工程(CQL-M/1)和/或奥迪材料工程 (I/GQ-3)商定后可进行厚层KTL(D-KTL) ...
–Corrosion resistance requirements (corrosion cycle test) for Ofl-x330 changed –Applicable documents updated Always use the latest version of this standard.This electronically generated standard is authentic and valid without signature.The English translation is believed to be accurate. In case of ...
Ofl-x1 00, Ofl-x300, Ofl-x600 Pretreatment not specified (not possible for manufacturing reasons), single-layer liquid paint according to any method, alternatively cathodic dip paint. Ofl-x1 30, Ofl-x330 Zinc phosphated, Fe or Mn phosphated, single-layer liquid paint according to any method,...
–Corrosion resistance requirements (corrosion cycle test) for Ofl-x330 changed –Applicable documents updated Always use the latest version of this standard.Page 1 of 11 This electronically generated standard is authentic and valid without signature.The English translation is believed to be accurate. ...
No. Property Ofl-x100 Ofl-x130 Ofl-x300 Ofl-x330 Ofl-x600 Ofl-x630 Ofl-x631 Ofl-x634 1 Corrosion behavior 1) 1.1 After aging in salt spray fog according to DIN 50021-SS 1.1.1 48 h without scribe mark 2) no blisters, no base ...
有选择地进行阴极浸渍涂漆(KTL) 进行磷酸锌处理,阴极浸渍涂漆(KTL) 进行磷酸锌处理,双层涂漆(浸涂+喷涂) 进行磷酸锌处理,厚层的阴极浸渍涂漆或者 KTL+浸涂(用于极强劲地施加负荷的零件,例如发动机室前端零件 Ofl –x100, Ofl –x300 Ofl –x600 Ofl –x130 Ofl –x330 Ofl –x630 Ofl –x631 Ofl –x634 ...
Ofl-x330替代性预处理(基于氧化锆),磷酸锌、铁磷酸盐 处理或锰磷酸盐处理或三价磷酸盐处理; 单层-湿法涂漆方法不限,有选择地进行阴极浸渍 涂漆(KTL)(例如传动轴) Ofl-x630磷化锌或三价磷酸盐,KTL; 与大众工程(CQL-M/1)和/或奥迪材料工程 (I/GQ-3)商定后可进行厚层KTL(D-KTL) ...