Ofl-r672 Ofl-r673 Ofl-r677 As r642, but with additional lubricant treatment (see VW 011 10) Zinc/nickel coating, deposited from alkaline electrolytes, black Cr(VI)-free passivated Zinc/nickel coating, deposited from alkaline electrolytes, black Cr(VI)-free ...
TL_244_EN Group standard TL 244 Issue 2017-06 Class. No.:50204 Descriptors:zinc, nickel, passivation, sealing, chromium (VI)-free, Cr(VI)-free, corrosion protection, surface protection, alloy coating, Ofl-r642, Ofl-r643, Ofl-r645, Ofl-r649, Ofl-r672, Ofl-r673, Ofl-r677 Zinc/...
Ofl-r677同Ofl-r673,但是须另外按TL5213作润滑剂处理 3.2基本要求 首次供货和更改的认可按VW01155 避免有害物质按VW91101 进行一次完整的试验需要10个成品件。 注1:采用封闭剂的表面保护类型,可能影响涂胶的附着性能。 由于其微裂性,这些涂覆层也不适合于诸如空调装置的供气系统的密封元件,采用这种涂覆方法的部 ...
Ofl-r649a)锌/镍—涂覆层,从弱酸电解质中离析,银色,钝化处理,和封闭处理(仅用于铸件,例如:制动钳)Ofl-r672锌/镍—涂覆层,从碱性电解质中离析,黑色钝化处理,优先适用于黑色涂覆保护类型(MKL)和全周涂覆保护类型(KLR)Ofl-r673锌/镍—涂覆层,黑色钝化处理,且另外作封闭处理Ofl-r677同Ofl-r673,但是须另外按...
(VI),防腐蚀,表面保护锌/镍-合金涂覆层表面保护要求旧版本TL 244: 1987-10, 1992-05, 1993-11, 1995-12, 2002-05, 2004-12, 2006-08, 2007-02变更相对于 TL244: 2007-02 版本,作了如下更改:--补充了热处理后零件的抗拉强度≦ 1200Mpa 部分;--添加了 Ofl-r647 和 Ofl-r648 两种涂覆方法;--原...