TL233_带有覆盖护层的非电锌涂层表面保护要求_2003_中
(see table 1), a distinction is made between four surface protection types for the coating system as per this standard, which are desig‐ nated with the following codes as per the specifications in Volkswagen standard VW 13750, sec‐ tion "Designation": Ofl-t330 Ofl-t350 Ofl-t630 Ofl-t650...
t630带有含润滑剂保护层的锌涂层不含CrVI黑色1受光照安装部位的替换件例 如行走机构范围内的零部件标准表面防护标准表面防护标准表面防护标准表面防 护黑色黑色黑色黑色1111用于公制用于公制用于公制用于公制ISOISOISO ISO––––螺纹的螺纹件以及具有抗拉强螺纹的螺纹件以及具有抗拉强螺纹的螺纹 ...
If, however, the coating is a color coating, this must be specified in the drawing (e.g. Ofl-t630, blue). 3.2 General requirements Approval of first supply and changes according to VW 011 55. Avoidance of hazardous substances according to VW 911 01. Design and process assurance acc. to...
内容提示: Group standard TL 233Issue 2018-07Class. No.: 50223Descriptors: aluminum flake, base coat, corrosion protection, organic coating, surface protection, t330, t350, t630,t650, top coat, zinc, zinc flakeNon-Electrolytically Applied Zinc Flake Coatings with an Organic Top CoatSurface ...
大众 TL-233 2010中文版 非电解质涂覆的锌涂层和保护层 表面防护要求 以前的版本 TL 233: 1982-09, 1983-02, 1991-05, 1992-06, 1993-11, 1998-02, 2003-09, 2003-11 更改 相对于TL233：2003-11 版本，已作了如下更改：1、适用范围已更改：最高适用温度改为180°C，新增规范TL 180；2、表1和表2...
3.7.2 对于Ofl-t630 和Ofl-t650 的技术要求 对于螺纹零件,只需对其头部和/或表面及扳手平面进行涂覆。 涂层最小厚度为10μm (其中锌涂层≥3μm) 。 涂层最大厚度为 25μm.如果要具备比基本要求更高的防腐蚀能力,例如弹簧夹箍卡子(详见第 3.9.2.4 章节),也可以有更高的涂层厚度。 3.8 粘附性和延展性 ...
如果对涂层颜色有要求,则必须在图纸上附加说明(例如,Ofl-t630,蓝色)。3.2基本技术要求首次供货和更改的批准按VW01155避免有害物质按VW91101一次完整的试验需要试样约10件(取决于尺寸大小)。如果是细小的零件,例如连接件,于一次试验性生产的首次样品供货,试件50kgo所使用的涂覆对象和涂层都不得含有Cr(VI)化合物。
Ofl-t630 Zinc flake coating a) with top coat containing lubricant, black b) ; for use in exposed installation positions; e.g. in body. Ofl-t650 Zinc flake coating a) with top coat, black b) ; for use in exposed installation positions; ...
TL233_带有覆盖护层的非电锌涂层表面保护要求_2003_中