ThefollowingchangeshavebeenmadeascomparedtoTL244:1995-12: - IntroductionofCr(VI)-freeconversionlayersonthebasisoftheEnd-of-LifeVehiclesDirective oftheEuropeanUnion(AltautoV)(seetable2) Ofl-r640replacedbyOfl-r642andOfl-r643 SealingforOfl-r645notpermittedanymore ...
TL_244_EN Group standard TL 244 Issue 2017-06 Class. No.:50204 Descriptors:zinc, nickel, passivation, sealing, chromium (VI)-free, Cr(VI)-free, corrosion protection, surface protection, alloy coating, Ofl-r642, Ofl-r643, Ofl-r645, Ofl-r649, Ofl-r672, Ofl-r673, Ofl-r677 Zinc/...
Ofl-r643锌/镍-涂覆层,钝化处理,另外作封闭处理(外观为银色至淡蓝彩虹光) Ofl-r645同Ofl-r642,但是须另外按TL52132作润滑剂处理 Ofl-r647锌/镍-涂覆层,钝化处理(可弯曲锌/镍—涂覆层,银色至单) Ofl-r648 如Ofl-r647,但又利用浸泡或旋转的方法增加了两层含铝材质镀层(类 ...
(VI),防腐蚀,表面保护锌/镍-合金涂覆层表面保护要求旧版本TL 244: 1987-10, 1992-05, 1993-11, 1995-12, 2002-05, 2004-12, 2006-08, 2007-02变更相对于 TL244: 2007-02 版本,作了如下更改:--补充了热处理后零件的抗拉强度≦ 1200Mpa 部分;--添加了 Ofl-r647 和 Ofl-r648 两种涂覆方法;--原...
(VI),防腐蚀,表面保护锌/镍-合金涂覆层表面保护要求旧版本TL 244: 1987-10, 1992-05, 1993-11, 1995-12, 2002-05, 2004-12, 2006-08, 2007-02变更相对于 TL244: 2007-02 版本,作了如下更改:--补充了热处理后零件的抗拉强度≦ 1200Mpa 部分;--添加了 Ofl-r647 和 Ofl-r648 两种涂覆方法;--原...