aThree specimens are tested and the dimensions of tensile test specimens are shown in Figure 1. The gauge section is 6.35±0.13mm in diameter by 25.4mm long. The minimum R is 15mm.The final surface finish of gauge section of specimen is 0.81μm. 三个标本被测试,并且维度拉伸试验试棒在表1...
A tensile test helps determining tensile properties such as tensile strength, yield point or yield strength, % elongation, % reduction in area and modulus of elasticity. Since mechanical properties are to some extent influenced by the size and shape of the test specimen, it is customary to use...
It was investigated the size effects of test specimen on the fracture behaviour and apparent strength of SiC/SiC tubes in order to minimize the size of test specimen, as well as to develop circumferential tensile test method for SiC/SiC fuel cladding of nuclear reactor. The tube specimens with...
The mechanical characteristics which are directly found out from tensile test are ultimate tensile strength, maximum elongation, yield strength, maximum force, and area reduction. Table 2.7 shows the standard tensile specimen size and its different dimensions along with acceptable tolerances as per the ...
Figure 1. Standard Tensile Test Configuration To perform the test, the grips of the testing apparatus hold the specimen firmly at the wide ends. Because the middle of the sample is narrower than the ends, the stress is concentrated in that area so that fracture and most of the strain occur...
On the size-dependent behavior of the micro-wire in the micro-tensile test To evaluate the size effect, we focused on the relation between the strength and the specimen diameter. Our result shows that the strength of the ... S Ko,B Jung,H Lee,... - 《Proceedings of Spie the Internati...
tensile load test 拉力负载试验 相似单词 face bend[test]specimen 面弯试样 specimen n.[C,U] 样品,标本,试料 tensile a. 1.拉力的,张力的,抗张的 2.可伸展的;可拉长的;可延展的 tensile strength 拉伸强度 tensile socket 张拉索接 specimen box 标本盒 test n.[C] 1.试验 2.化验;化验法...
The splitting tensile test, also known as indirect tensile strength test, captures the peak compressive load applied transversely to a cylindrical specimen prior to or on the onset of cracking, and therefore does not necessarily reflect the material's post-peak behaviour. ...
This relation enables to convert the test results obtained on specimens of different sizes and shapes to the strength of the basic size specimen. This is important for the test results obtained on samples taken from finished structures, as these samples are usually of different sizes. 展开 ...
Sample Size Capacity Range from 25 grams to 1,000,000 lbs. Capability to Test Variety of Tensile and Specimen Types On-Site Machine Shop and Specimen Preparation Ability to Test Metals, Alloys, Composites, Polymers, Ceramics, Plastics, Wood and More ...