Super-absorbent hydrogelSwelling ratioWater retention capabilitySuper-absorbent hydrogels (SAH) have become the focus of attention due to their broadly applications in many areas like agriculture, wastewater treatment and hygienic products. Swelling ratio (SR), swelling rate and water retention capacity ...
1) swelling ratio 溶胀比1. The effects of reaction temperature,the amount of AM monomer,cross - linking agent, and initiator on the swelling ratio of the hydrogel were investigated. 考察了介质的离子浓度、pH值和温度对水凝胶溶胀比的影响,结果表明,离子浓度越大,水凝胶的溶胀比越小;水凝胶具有一定...
1.The effects of reaction temperature,the amount of AM monomer,cross - linking agent, and initiator on theswelling ratioof the hydrogel were investigated.考察了介质的离子浓度、pH值和温度对水凝胶溶胀比的影响,结果表明,离子浓度越大,水凝胶的溶胀比越小;水凝胶具有一定的pH可逆性。 2.The experiment s...
The obtained results show a strong influence of the swelling ratio of the gel on the magnitude of both concentration and diffusion coefficient of the examined probes. While the drop in the value of the diffusion coefficient with a decrease in the swelling ratio is not surprising (the denser pol...
4.The effect of temperature and pH on the swelling ratio of intelligent hydrogel温度和pH值对智能水凝胶溶胀行为的影响 5.Swelling Degrees Property of High Strength PAMPS-PAAm Interpenetrating Polymer Network Hydrogel高强度PAMPS-PAAm互穿网络凝胶及其溶胀性能 ...
The equilibrium swelling ratio of hydrogel was... Z Peng,F Chen - 《International Journal of Polymeric Materials & Polymeric Biomaterials》 被引量: 48发表: 2010年 Effect of Peptide Loading and Surfactant Concentration on the Characteristics of Physically Crosslinked Hydrogel. (2000) Effect of ...
Similar to the PAM single-network hydrogel, the swelling ratio of the SSH increased by ~50% after implantation for 30 min, which further increased to ~85% with the time extending to 1 h. Remarkably, the compressive modulus of the SSH grew from 16.2 ± 0.5 to 18.9 ± ...
swelling ratio 美 英 un.膨胀比;泡胀率 网络溶胀比;膨润度;膨胀率 英汉 网络释义 un. 1. 膨胀比 2. 泡胀率
The swelling ratio of hydrogel using polyglycerol as plasticizer was significantly higher than that of using glycerol. The longer the heating time of the cross-linked could reduce the swelling ratio. The process temperature did not affect the swelling ratio. 展开 关键词: Swelling properties poly(...
in the hydrogel was observed to greatly enhance various properties, including gel fraction, swelling ratio, porosity, drug loading, and drug release percent... M Priyanka,S Poonam,SG Warkar - 《Colloid & Polymer Science》 被引量: 0发表: 2024年 Optimization Of Swelling, Drug Loading And Releas...