V. Kain, Stress corrosion cracking (SCC) in stainless steels, in Stress corrosion cracking, Theory and practice, Edited by: Raja, V. S. and Shoji, T., Oxford, Cambridge, Philadelphia, New Delhi, (2011), 199-244.V. Kain, Stress corrosion cracking (SCC) in stainless steels, in Stress ...
介绍:The National Physical Laboratory is operated on behalf of the DTI by NPL Management Limited, a wholly owned subsidiary of Serco Group plc Stress Corrosion Cracking Guides to Good Practice in Corrosion Control 2295/aaron/IK/0004 Contents page Introduction 1 What causes stress corrosion cracking?
There is ample evidence that these steels can be used under circumstances where the austenitic types would fail.doi:10.1179/imtr.1981.26.1.301TrumanJ. E.Taylor & FrancisMetallurgical ReviewsJ. E. Truman, “Stress corrosion cracking of martensitic and ferritic stainless steels,” Int. Metals Rev.,...
The mechanism of hydrogen-induced slow crack growth (SCG) of types 321 and 310 steels and stress corrosion cracking (SCC) of type 321 steel in boiling MgCl//2 solution were investigated. The tracing observation showed that the plastic zone ahead of a loaded notched tip of austenitic stainless...
chlorides for stainless steel, ammonia for copper, and H2S for low-carbon steel. Residual thermal stresses, or those induced by bending electrical lead wires, in combination with moisture serve to promote such cracking. When the loading is cyclic rather than static, the stress-corrosion damage is...
aStress corrosion cracking (SCC) and hydrogen embrittlement (HE) of sensitized stainless steels of types 304, 310 and 316 were investigated as a function of applied stress at different test temperatures in boiling saturated magnesium chloride (MgCl2) solutions under a constant applied stress condition...
Resistance to external stress corrosion cracking (ESCC) and crevice corrosion were examined for various candidate canister materials in the spent fuel dry storage condition using concrete casks. A constant load ESCC test was conducted on the candidate materials in air after deposition of simulated sea...
2.Thestress corrosion crackcauses of high sulfur pipes serviced hydrodesulfurization system of a refinery were analyzed.表明管道的开裂是由富含H_2S环境介质再加上焊缝附近较高的焊接残余应力引起的应力腐蚀开裂。 3.The susceptibility tostress corrosion cracking (SCC) of the welded joint of X80 pipeline s...
The selection of a stress corrosion cracking (SCC) test which procures a reliable classification of stainless steels with regard to their SCC resistance in chloride media requires the choice of a suitable electrolyte in which the passive film is similar to those built in industrial conditions and ...
light water reactor (LWR) environmentsThis chapter focuses on stress corrosion cracking (SCC) of austenitic stainless steels in high temperature light water reactor (LWR) environments, and emphasizes common grades of wrought austenitic stainless steel over cast, ferritic or martensitic stainless steels. ...