本发明具有优良的综合力学性能,屈服强度不小于700MPa,适合钢板减薄设计;耐候性为普通钢材的2～8倍;生产工艺简单,生产周期短,钢材成本较低. The present invention has excellent mechanical properties, yield strength of not less than 700MPa, for thinning steel design; weather resistance 2-8 times that of ...
High-Quality Material: The PHD PQ Steel Drill Rod is crafted from ZT850 carbon steel, ensuring exceptional strength and durability for demanding ore mining applications. Reliable Yield Strength: With a yield strength of 1030-1040 Mpa, this drill rod provides a high level of resistance to deformat...
Tensile strength represents the material’s ability to resist breaking under tension. It is also measured in units of force per unit area (such as psi or MPa). In summary, the key difference between tensile strength and yield strength lies in their definitions and what they represent during ma...
asteel with a minimus yield strength of 620 MPa(90,000PSI) 钢以minimus出产量620 MPa (90,000PSI) [translate] 英语翻译 日语翻译 韩语翻译 德语翻译 法语翻译 俄语翻译 阿拉伯语翻译 西班牙语翻译 葡萄牙语翻译 意大利语翻译 荷兰语翻译 瑞典语翻译 希腊语翻译 51La ...
550MPa Yield Strength G550 Gi Galvanized Steel Zinc Coated, Find Details and Price about Galvanized Steel Coil Galvanized Steel from 550MPa Yield Strength G550 Gi Galvanized Steel Zinc Coated - Tianjin Runfei Trade Co., Ltd
The low-temperature engineering steel with yield strength not lower than 550MPa disclosed by the invention is not only capable of producing a steel plate with the thickness bigger than 80mm; the steel plate is uniform in tissue performance in the thickness direction, better in low-temperature ...
Since flattened steel sheets often show the unexpectedly lower or higher yield strength than leveled sheets, unceasing efforts have been made to accurately predict the yield strength in pipe-forming industries. In the present investigation, the yield strength of line-pipe or casing-pipe steels was ...
Material Yield strength (MPa) Ultimate strength (MPa) Density (g/cm³) ASTM A36 steel 250 400 7.8 Steel, API 5L X65 (Fikret Mert Veral) 448 531 7.8 Steel, high strength alloy ASTM A514 690 760 7.8 Steel, prestressing strands 1650 1860 7.8 Piano wire 2200–2482[5] 7.8 High ...
Section Shape ROUND Surface Treatment Polished Tolerance ±1% Oiled or Non-oiled Slightly Oiled Invoicing by actual weight Other attributes Place of Origin Shandong, China Alloy Or Not Non-Alloy Standard AISI ASTM Grade 4130 4140 Delivery Time ...
The invention relates to 800MPa-grade (yield strength) quenched-tempered high-strength steel and a production method thereof. The steel comprises the following components in percentage by weight: 0.07-0.15% of C, 0.10-0.30% of Si, 0.80-1.60% of Mn, 0.20-0.70% of Cr, 0.10-0.40% of Mo,...