Ultimate Strength Yield Point X 1000/in2 Modulus of Elasticity (T) Tension X 1000/in2 Compression, in terms of T Shear in terms of T in Tension (E) x 106 psi in Shear, in terms of E Cast iron, grey, class 20 20a 3.6 T - 4.4 T 1.6 T ... 11.6 0.40 E class 25 25a 3.6...
Specific Gravity: 7.75 Modulus of Elasticity: 30 x 106 psi (207GPa) Machinability: 65-70% of a 1% carbon steelHeat Treating InstructionsHardeningCritical Temperature: Ac1: 1410°F (766°C)Preheating: Heat at a rate not exceeding 400°F per hour (222°C per hour). For complex and large...
Modulus of Elasticity Tension 31 8620 SteelMechanical Properties PropertiesMetricImperial Tensile strength530 MPa76900 psi Yield strength385 MPa55800 psi Elastic modulus190-210 GPa27557-30458 ksi Bulk modulus (typical for steel)140 GPa20300 ksi ...
屈服强度(屈服极限)(Tensile Strength, Yield):≥205 MPa(29700 psi)(@Strain 0.2%) 断裂延伸率(Elongation at Break):≥40% 断面收缩率(Reduction of Area):≥50% 弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 泊松比(Poissons Ratio):0.29 剪切模量(Shear Modulus):77.0 GPa(11200 ksi) 热性能(Th...
屈服强度(屈服极限)(Tensile Strength, Yield):240 MPa(34800 psi) 断裂延伸率(Elongation at Break):55% 弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear): 16.0 μm/m-℃(@Temperature 0-100 ℃) 16.2 μm/m-℃(@Temperature 0-315 ℃) 17.5...
Specific Gravity: 7.83 Modulus of Elasticity: 31 x 106 psi (214GPa) Machinability: 85-90% of a 1% carbon steelHeat Treating InstructionsHardeningCritical Temperature: Ac1: 1350°F (732°C) Ac3: 1400°F (760°C) Ar1: 1295°F (703°C) Ar3: 1240°F (671°C)Preheating: Heat at a ...
Modulus of Elasticity 0.294 lb/in3 (8138 kg/m3) Thermal conductivity 24 Btu/ft/hr/°F 41.5 W/m/°K Machinability 65% of a 1% carbon steel AISI M2 Tool Steels Properties Mechanical Mechanical properties Metric Imperial Hardness, Rockwell C (tempered at 1150°F, quenched at 2200°F) 62 ...
Tensile Strength, Yield 310 MPa 45000 psi Elongation at Break (in 50 mm) 16.0 % 16.0 % Reduction of Area 40.0 % 40.0 % Modulus of Elasticity (Typical for steel) 200 GPa 29000 ksi Bulk Modulus (Typical for steel) 140 GPa 20300 ksi Poissons Ratio (Typical For Steel) 0.290 0.290 Shear ...
E = modulus of elasticity, pounds per square inch (psi) Steel: E = 29,000,000 psi = 29 (10)6. Stainless Steel: E = 28,000,000 psi = 28 (10)6. Aluminum: E = 10,000,000 psi = (10)7. F = allowable fiber unit stress, psi ...
Ultimate Tensile Strength 58,000 – 79,800 psi 400 – 550 MPa Yield Tensile Strength 36,300 psi 250 MPa Elongation at Break (in 200 mm) 20.0% 20.0% Elongation at Break (in 50 mm) 23.0% 23.0% Modulus of Elasticity 29,000 ksi 200 GPa Bulk Modulus (Typical for steel) 20,300 ksi 140...