屈服强度(屈服极限)(Tensile Strength, Yield):215 MPa(31200 psi) 断裂延伸率(Elongation at Break):70% 弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 泊松比(Poissons Ratio):0.29 剪切模量(Shear Modulus):77.0 GPa(11200 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear):17.3 μm/m-℃...
Modulus of Elasticity, Young's Modulus For Common Engineering Materials TableEngineering Metals and Materials Table of Contents The following chart gives ultimate strength, yield point and modulus of elasticity data for steel and iron. Engineering Material...
屈服强度(屈服极限)(Tensile Strength, Yield):240 MPa(34800 psi) 断裂延伸率(Elongation at Break):55% 弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear): 16.0 μm/m-℃(@Temperature 0-100 ℃) 16.2 μm/m-℃(@Temperature 0-315 ℃) 17.5...
Modulus of elasticity 26000 ksi Heat 0.427J/g·℃ Thermal conductance 22W/m·℃ Melting point 1300 - 1350 ℃ Thermal expansion coefficient in./in./ ℉ x 10-6 70-200 F 7.7 70 - 400 F 8.6 70 - 800 F 8.9 70 - 1000 F 9.1
MECHANICAL PROPERTIES FOR STEEL STRUCTURAL PLATE MATERIAL fu Minimum Tensile Strength (psi) fy Minimum Yield Point (psi) Em Modulus of Elasticity (psi) 45,000 33,000 29 x 106 Note: Material requirements based on AASHTO M 167 Thickness (Inches) 0.100 0.125 0.150 0.175 0.200 0.225 0.250 TABLE ...
Reduction of Area40.0 %40.0 % Modulus of Elasticity (Typical for steel)205 GPa29700 ksi Bulk Modulus (Typical for steel)140 GPa20300 ksi Poissons Ratio (Typical For Steel)0.2900.290 Machinability (Based on AISI 1212 steel. as 100% machinability)70 %70 % ...
TEMPERYield Strength (ksi)Ultimate Tensile Strength (ksi)Modulus of Elasticity (ksi)Brinell Hardness (500km/10mm) Annealed 67 81 30,000 220 Quenched and Tempered 140 150 30,000 300 Normalized 64 97 30,000 200 Steel Parts Gallery Click to enlarge ...
TEMPERYield Strength (ksi)Ultimate Tensile Strength (ksi)Modulus of Elasticity (ksi)Brinell Hardness (500km/10mm) Annealed and Cold Drawn 84 99 30,000 200 Cold Drawn 83 97 30,000 190 Hot Rolled 48 88 30,000 180 Steel Parts Gallery ...
Modulus of Elasticity Tension 31 8620 Steel Mechanical Properties Properties Metric Imperial Tensile strength 530 MPa 76900 psi Yield strength 385 MPa 55800 psi Elastic modulus 190-210 GPa 27557-30458 ksi Bulk modulus (typical for steel) 140 GPa 20300 ksi Shear modulus (typical for steel) 80 GPa...
Modulus of Elasticity:30 x 106 psi (207GPa) Machinability:50-60% of a 1% carbon steel AISI M2 Tool Steels Properties Mechanical Mechanical properties Metric Imperial Hardness, Rockwell C (tempered at 1150°F, quenched at 2200°F) 62 62 Hardness, Rockwell C (as hardened, quenched at 2200°...