Recent Research and Developments in Cold-Formed Steel Design and ConstructionMahendran, M. (1996), "Is the modulus of elasticity of steel 200 GPa?" , Proc of the 13th International Specialty Conference on Cold-formed Steel Structures, St. Louis, MO, USA, 641-648....
弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 泊松比(Poissons Ratio):0.29 剪切模量(Shear Modulus):77.0 GPa(11200 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear):17.3 μm/m-℃(@Temperature 0-100℃) 17.8 μm/m-℃(@Temperature 0-315℃) 18.7 μm/m-℃(@Temperature 0-650℃...
Ultimate Strength Yield Point X 1000/in2 Modulus of Elasticity (T) Tension X 1000/in2 Compression, in terms of T Shear in terms of T in Tension (E) x 106 psi in Shear, in terms of E Cast iron, grey, class 20 20a 3.6 T - 4.4 T 1.6 T ... 11.6 0.40 E class 25 25a 3.6...
Modulus of elasticity (@20°C/68°F) 215 GPa 31200 ksi Poisson’s ratio 0.27-0.30 0.27-0.30 5. Forging of H13 Tool Steel Heating for forging must be done slowly and uniformly. Soak through at 1900°-2000°F and reheat as often as necessary, stopping work when the temperature drops belo...
Modulus of elasticity190-210 GPa Bulk modulus (Typical for steel)140 GPa Shear modulus (Typical for steel)80 GPa Poissons ratio0.27-0.30 Elongation at break (in 50 mm)21.50% Reduction of area59.6 Hardness, Brinell217 Hardness, Knoop (Converted from Brinell hardness)240 ...
弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear): 16.0 μm/m-℃(@Temperature 0-100 ℃) 16.2 μm/m-℃(@Temperature 0-315 ℃) 17.5 μm/m-℃(@Temperature 0-540 ℃) 比热容(Specific Heat Capacity):0.500 J/g-℃(@Temperature 0-100...
Temperature (°C)Modulus of elasticity (GPa)Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) andThermal conductivity (W/m·°C)Specific thermal capacity (J/kg·°C)Specific electrical resistivity (Ω mm²/m)Density (kg/dm³)Poisson's coefficient, ν 3...
For this purpose it is helpful to assume the soil as elastic and to consider the classical problem of a flexible strip or beam on an elastic foundation. 9.3.3.2.2 Soil Stiffness The modulus of elasticity of an elastic material E is defined as: (9.17)E=σ/ɛ The units of E are ...
Specific Gravity: 7.83 Modulus of Elasticity: 31 x 106 psi (214GPa) Machinability: 85-90% of a 1% carbon steelHeat Treating InstructionsHardeningCritical Temperature: Ac1: 1350°F (732°C) Ac3: 1400°F (760°C) Ar1: 1295°F (703°C) Ar3: 1240°F (671°C)Preheating: Heat at a ...
Modulus of elasticity 190-210 GPa 27557-30458 ksi Bulk modulus (Typical for steel) 140 GPa 20300 ksi Shear modulus (Typical for steel) 80 GPa 11600 ksi Poissons ratio 0.27-0.30 0.27-0.30 Elongation at break (in 50 mm) 21.50% 21.50% Reduction of area 59.6 59.60% Hardness, Brinell 217 ...