Modulus of Elasticity Tension 31 8620 SteelMechanical Properties PropertiesMetricImperial Tensile strength530 MPa76900 psi Yield strength385 MPa55800 psi Elastic modulus190-210 GPa27557-30458 ksi Bulk modulus (typical for steel)140 GPa20300 ksi ...
Elastic modulus 190-210 GPa 27557-30458 ksi M2 Steels Thermal Properties Thermal properties Metric Imperial CTE, linear (@20.0 – 100°C/ 68.0 – 212°F) 10 μm/m°C 5.56 μin/in°F CTE, linear (@20.0 – 500°C/68.0 – 932°F) 12.2 μm/m°C 6.78 μin/in°F CTE, linear (...
Elastic (Young's, Tensile) Modulus 190 GPa 27 x 106 psi Elongation at Break 12 % Fatigue Strength 1160 MPa 170 x 103 psi Poisson's Ratio 0.29 Shear Modulus 72 GPa 10 x 106 psi Shear Strength 1330 MPa 190 x 103 psi Tensile Strength: Ultimate (UTS) 2220 MPa 320 x 103 psi Tensile ...
Elastic (Young's, Tensile) Modulus 200 GPa 29 x 106 psi Elongation at Break 28 % Fatigue Strength 370 MPa 54 x 103 psi Poisson's Ratio 0.28 Rockwell C Hardness 22 Shear Modulus 78 GPa 11 x 106 psi Shear Strength 450 MPa 65 x 103 psi Tensile Strength: Ultimate (UTS) 690 MPa 100 ...
Elastic modulus 190-210 GPa 27557-30458 ksi HEAT TREATING INSTRUCTIONS HARDENING HSS SKH9 / SKH51 Preheating: To minimize distortion and stresses in large or complex tools use a double preheat. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1100°F (593°C) equalize,...
Yield strength 415 MPa 60200 psi Bulk modulus (typical for steel) 140 GPa 20300 ksi Shear modulus (typical for steel) 80 GPa 11600 ksi Elastic modulus 190-210 GPa 27557-30458 ksi Poisson's ratio 0.27-0.30 0.27-0.30 Elongation at break (in 50 mm) 25.70% 25.70% Hardness, B...
Tensile strength 385 MPa 55800 psi Yield strength 325 MPa 47100 psi Bulk modulus (typical for steel) 140 GPa 20300 ksi Shear modulus (typical for steel) 80.0 GPa 11600 ksi Elastic modulus 190-210 GPa 27557-30458 ksi Poisson's ratio 0.27-0.30 0.27-0.30 Elongation at break (In 50 mm) 18.0...
Tensile strength 655 MPa 95000 psi Yield strength 415 MPa 60200 psi Bulk modulus (typical for steel) 140 GPa 20300 ksi Shear modulus (typical for steel) 80 GPa 11600 ksi Elastic modulus 190-210 GPa 27557-30458 ksi Poisson's ratio 0.27-0.30 0.27-0.30 Elongation at break (in 50 m...
Yield strength (@strain 0.200 %) 350 MPa 50800 psi Elastic modulus 193 GPa 27992 ksi Poisson’s ratio 0.300 0.300 Elongation at break (in 50 mm) 47% 47% Other Designations Equivalent materials to grade 301LN stainless steel are given below. ASTM A666 JIS G4305 EN 10088-2 EN 1.4318 JIS...
Tensile strength 655 MPa 95000 psi Yield strength 415 MPa 60200 psi Bulk modulus(typical for steel) 140 GPa 20300 ksi Shear modulus (typical for steel) 80 GPa 11600 ksi Elastic modulus 190-210 GPa 27557-30458 ksi Poisson's ratio 0.27-0.30 0.27-0....