fracture propertiesLiquid lithium, which is under consideration as blanket fluid of fusion reactors, is more corrosive against austenitic and martensitic-ferritic steels than liquid sodium. The results of corrosion studies in flowing lithium as well as of tests on the mechanical behaviour of the ...
B. Mechanical properties of nitrogen-rich surface layers on SS304 treated by plasma immersion ion implantation [Text] / B. B. Fernandes, S. Mandl, R. M. Oliveira, M. Ueda // Applied Surface Science. - 2014. - Vol. 310. - P. 278-283. doi: 10.1016/j.apsusc.2014.04.142...
Microstructure and Mechanical Properties of 10CrNi3MoV Steel-SS304L Composite Bimetallic Plates Butt Joint by Shielded Metal Arc Welding10CrNi3MoV steel304L stainless steelbimetallic platesdissimilar metal weldingmicrostructuremechanical propertieswelding joint...
This paper will highlight the methods employed for evaluating the mechanical properties of the irradiated cladding and wrapper and discuss the trends in properties as a function of dpa (displacement per atom) and irradiation temperature. 展开
From the correlation between the microstructural and mechanical properties, shear strength of approximately 35MPa for graphite-304SS-brazed joint produced at 900°C was demonstrated. After the shear tests, the fracture surfaces were analyzed by SEM-EDS. 展开 ...
Table 2. Mechanical properties of grade 630 stainless steels Condition Tensile Strength (MPa) Yield Strength 0.2% Proof (MPa) Elongation (% in 50mm) Hardness Rockwell C (HR C) Brinell (HB) Solution Treated 1105 typ 1000 typ 15 typ 38 max 363 max Condition 900 1310 min 1...
Table 2. Mechanical properties of grade 630 stainless steels Condition Tensile Strength (MPa) Yield Strength 0.2% Proof (MPa) Elongation (% in 50mm) Hardness Rockwell C (HR C) Brinell (HB) Solution Treated 1105 typ 1000 typ 15 typ 38 max 363 max Condition 900 1310 ...
Table 2. Mechanical properties of grade 630 stainless steels Condition Tensile Strength (MPa) Yield Strength 0.2% Proof (MPa) Elongation (% in 50mm) Hardness Rockwell C (HR C) Brinell (HB) Solution Treated 1105 typ 1000 typ 15 typ 38 max 363 max Condition 900 1310 min 1170 min 10 m...
within closed dies positioned between the plates of a hydraulic press.The applied pressure and instant contact of the molten metal with the die surface produce a rapid heat transfer condition that yields a pore-free fine-grain casting with mechanical properties approaching...
410 stainless steel Mechanical Properties Tempering Temperature (°C) Tensile Strength (MPa) Yield Strength 0.2% Proof (MPa) Elongation (% in 50mm) Hardness Brinell (HB) Impact Charpy V (J) Annealed * 480 min 275 min 16 min – – 204 1310 1000 16 388 30 316 1240 960 14 325...