annealing twinsecondary twingrain orientation304 不锈钢织构退火孪晶二次孪晶晶粒取向The texture evolution, twin crystallographic nature and grain orientation variation during the solution heat treatment process of the 304 stainless steel pipe were studied. It was found that after the solution heat treatment...
The corrosion elongation curves for type 304 stainless steel at an applied stress of 300 MPa subjected to different cold reductions and subsequent solution annealing treatments at 1050 °C for 60 min are shown in Fig. 4. The elongation curve for the reference sample that was solution annealed wi...
The weight loss of all the steels increased with the increasing corrosion time. As a conclusion, the steel solution treated at 1100 ℃ for 0.5 h exhibited a comprehensive performance. 展开 关键词: 316L stainless steel solution annealing intergranular corrosion grain boundary ...
The influence of small defect clusters on irradiation-assisted stress corrosion cracking (IASCC) of austenitic stainless steels has been examined. A CP-304... JT Busby,MM Sowa,EA Kenik - 《Journal of Astm International》 被引量: 20发表: 2004年 Post-Irradiation Annealing of Dislocation Microstru...
aUnless specified otherwise, all austenitic stainless steel materials shall be furnished in a solution annealed condition. Approved repairs, if any, shall be made prior to solution annealing 除非另外说明,所有奥氏体的不锈钢的材料在解答锻炼的情况将被装备。 批准的修理,若有的话,在解答焖火之前将被进行...
aPM 304L and 316L stainless steel have been compacted at 400, 600 and 800 MPa and sintered in vacuum and in nitrogen–hydrogen atmosphere. Postsintered heat treatments (annealing solution and ageing at 375, 675 and 875 °C) have been applied. Pitting corrosion resistance has been studied using...
Bright Annealed (BA) pipe is produced by heat-treating (annealing) steel with a controlled atmosphere furnace. After heat-treatment, the steel has a reflective, mirror-like appearance, but may also have some imperfections and cloudiness. BA stainless steel can...
Bright Annealed (BA) pipe is produced by heat-treating (annealing) steel with a controlled atmosphere furnace. After heat-treatment, the steel has a reflective, mirror-like appearance, but may also have some imperfections and cloudiness. BA stainless steel can be buffed to ...
Effect of Cooling Rate on the Corrosion Behavior of As-Cast SAF 2205 Duplex Stainless Steel After Solution Annealing Treatment. Kuri, N.A. Mariano, Effect of cooling rate on the corrosion behavior of as-cast SAF 2205 duplex stainless steel after solution annealing treatment, ... CRONEMBERGER,...
Stainless steel ASTM 316 L is often used in the food industry as contact material with protein-rich dairy products. It has to be welded at some locations for many of these contact materials. This study aimed at i) determining any combined effects of the presence of whey protein (WP) and...