Using S2-glass fibre/FM94-epoxy unidirectional prepreg, GFRP plates were created. Drop weight impact tests were conducted at ambient (25 掳C), high (50, 75, 100 掳C), and low (25, 55 掳C) temperatures, as well as at various impact energies (75, 150, 225 J). The damages were ...
Here a simple method for fabrication of the microfluidic device with micro- and nanochannels was developed. The microchannels in micro and nano scales were fabricated on a glass substrate during a two- step process respectively. And then the glass substrate with the microchannels was bonded with an...
[58] performed low-velocity impact tests on E-glass fibre reinforced FM94 epoxy resin prepreg. In their work, it was found that over 90% of the impact energy was absorbed by the bending/shear deformation which resulted in delamination and matrix cracking. In a similar manner, the cross-ply...
The sheet-like prepreg gives a cured product having a glass transition temperature of −60° C. to 100° C. The curable composition includes one or more curable compounds (A) and at least one of a curing agent (B) and a curing catalyst (C). The curable compounds (A) include ...