The X-ray diffraction pattern (XRD) showed that the as-prepared sample was pure rutile TiO2. The field emission scanning electron microscopy (FESEM) images revealed that the RTNs exhibited a flower-like shape, with nanopetals ca. 60 nm in width and 15 nmin thickness. The high-resolution ...
XRD-TiO2-Rutile 下载积分:50 内容提示: 文档格式:PDF | 页数:1 | 浏览次数:14 | 上传日期:2018-12-07 07:32:19 | 文档星级: 阅读了该文档的用户还阅读了这些文档 6 p. GB/T 22038-2008 汽车轮胎静态接地压力分布试验方法 3 p. 函数单元测试(1)(第二章) 2 p. 议论文复习整理 1 p. ...
Figure1a,b shows the X-ray diffraction (XRD) pattern of epitaxial TiO2thin films grown on LaAlO3(001) and γ-sapphire (1\(\overline{1}\)02) single crystal substrates, respectively. The XRD results demonstrate that there is no secondary phase except for the anatase and rutile phase on the...
Published on Web 02/26/2009 Growth of Oriented Single-Crystalline Rutile TiO2 Nanorods on Transparent Conducting Substrates for Dye-Sensitized Solar Cells Bin Liu and Eray S. Aydil* Department of Chemical Engineering and Materials Science, Uni Versity of Minnesota, 421 Washington A Venue SE, Minnea...
ande. TiO2/VO2/TiO2heterostructure (scale bar = 5 nm) projected with [100] zone axis. Unlike the amorphous nature of TiOXfilms in homostructures (green square inc), obvious diffraction spots were observed in the FFT pattern of the TiO2films on VO2/TiO2(green square ine), and were...
A sample is known to contain two crystalline modifications of TiO2, namely rutile and anatase. Spectrographic analysis failed to reveal the presence of other elements, so the sample can be assumed to consist only of TiO2. A scan is made with the diffractometer and integrated intensities measured ...
However, the XRD pattern clearly shows that W5 exhibited anatase phase only (Supplementary Figure S1b). The weight percentage of rutile phase can be calculated from the individual diffraction peaks using a pre- viously reported method18. The phase contents of the samples can be estimated from ...
Preferentially oriented single crystalline rutile TiO2 was confirmed by the single peak in an XRD pattern (2 theta = 63, (0 0 2)). FESEM images evidenced the growth of an array of NRss having different geometries with respect to reaction time and solution refreshment rate. The length, ...
Simultaneous growth of 1D/3D-nanorod/nanoflower like structures of TiO2 on fluorine doped tin oxide (FTO) glass substrates has been achieved in one-step hydrothermal process. X-ray diffraction (XRD) pattern confirms the formation of rutile phase whereas enhanced light scattering in 1D/3D nanorod/...
The X-ray diffraction (XRD) pattern shows that TiO array is in rutile phase growing along the (002) direction. The field-emission scanning electron microscopy (FE-SEM) images of the samples indicate that the TiO array surface morphology and orientation are highly dependent on the synthesis ...