213837 PVA-g-PAA Substituted Benzimidazolium Group Membrane for Fuel Cell ApplicationsIn this work the focus has been on membrane and in an effort to replace the Nafion membrane, we synthesized the crosslinking agent 3-Amino -4-[3-(triethyl ammonium sulfonato) phenyl amino] phenylene (Compound...
具体方法取1g聚乙烯醇（PVA）溶解后加入6g丙烯酸(AA)混合均匀后，再加入0.001g左右的过硫酸钾（KPS）...
PVA-g-PAA based benzimidazolium group modified membranes for application in DMFCIn this work the focus has been on membrane and in an effort to replace the Nafion membrane, the compound 3-Amino -4-[3-(triethyl ammonium sulfonato) phenyl amino] phenylene (ATSPP) named as C2 was synthesized...
The Si/C anode using PVA‐g‐PAA binder, exhibits improved lithium storage properties and cycling stability than that of the parallel electrode with carboxymethyl cellulose binder, which exhibits an initial coulombic efficiency (82.0%), even a reversible capacity of 487 mAh g...
The Si/C anode using PVA-g-PAA binder, exhibits improved lithium storage properties and cycling stability than that of the parallel electrode with carboxymethyl cellulose binder, which exhibits an initial coulombic efficiency (82.0%), even a reversible capacity of 487 mAh g(-1) after 300 cycles...
A new water soluble polymer of poly(vinyl alcohol) (PVA) grafted with poly(acrylic acid) (PAA) is synthesized via a free‐radical polymerization of acrylic acid (AA) in a 1:1 weight ratio in PVA water solution. The Si/C anode using PVAゞ㏄AA binder, exhibits improved lithium storage ...
structureTGATwo types of hydrogels were synthesized by X-Ray irradiation of Poly-vinyl alcohol (PVA) and by using of cross-linking agent N,N'-methylene-bis-acrylamide for the synthesis of branched polymer Dextran-graft-Polyacrylaamide (D-g-PAA). Thermal characteristics of the samples were ...
PAA-g-PVA RAFT and MADIXLi, YaogongZhang, YaqinYang, DongFeng, ChunZhai, SujuanHu, JianhuaLu, GuolinHuang, Xiaoyu
The ZnO-g-C3N4 (6%)@PAA-g-(HEC/PVA)-Fe has higher swelling ratio (13.18 ± 0.51 g/g) after 6 h. However, it exhibited declined swelling ratio (5.86 ± 0.32 and 7.49 ± 0.42 g/g) at lower pH 3.0 and 5.0, respectively, and (13.48 ± 0.42 and 14.51 ± 0.42 g/g) at pH 9.0...
Two types of hydrogels were synthesized by X-Ray irradiation of Poly-vinyl alcohol (PVA) and by using of cross-linking agent N,N'-methylene-bis-acrylamide for the synthesis of branched polymer Dextran-graft-Polyacrylaamide (D-g-PAA). Thermal characteristics of the samples were measuredby TGA...