Modulus of elasticity (Gpa)ISO5270.35-0.5 Elongation at breakISO527150-350 Shore DDUROMETER52 Temperature range/-196-260 Coefficient of linear thermal expansionISO113591 Products available: Company introduction: Hongda was founded in 1999 and it is a professional manufaturer of high-perfor...
Modulus of elasticity on 23 °C 53457 N/mm 2 400 ‐ 800 Maximum bending stress on 23 °C 53452 N/mm 2 18 ‐ 20 Bending modulus of elasticity 53457 N/mm 2 600 ‐ 800 Ball impression hardness 132/60 53456 N/mm 2 25 ‐ 30
Modulus of elasticity (Gpa) ISO527 0.35-0.5 Elongation at break ISO527 150-350 Shore D DUROMETER 52 Temperature range / -196-260 Coefficient of linear thermal expansion ISO11359 1 Products available:1). PTFE skive Sheet (0.5-5mm thickness, special size can be customized) ...
Elongation at Break (Min %): 200% Modulus of Elasticity (GPa): 0.39 – 0.60 Flexural Modulus (GPa): 0.490 – 0.588 Coefficient of friction: 0.1 Electrical Volume Resistivity (Ω–cm): 1 × 10^14 – 1 × 10^19 Dielectric Constant 1 MHz: 2.1 Dielectric Strength (V/mil): 189 – 610 ...
Modulus of Elasticity0.412 GPa59.8 ksiCompressive; ASTM D695 Flexural Strength17.2 MPa2490 psiASTM D790 Flexural Modulus0.578 GPa83.8 ksiASTM D790 Compressive Yield Strength5.10 MPa740 psi1% Deformation; ASTM D695 15.1 MPa2190 psi10% Deformation; ASTM D695 ...
Modulus of ElasticityDIN 53482750 MPa Volume ResistivityDIN 534821018ΩCM Dielectric Constant (60Hz - 2GHz)ASTM D1502.1 Dielectric StrengthIEC 60243-1 Film 100µm105 Coefficient of Friction<0.1 Virgin PTFE Parts Virgin PTFE (unfilled) is most often used where mechanical properties are not the most...
Modulus of elasticity (tensile test) 667,000 psi 1 mm/min DIN EN ISO 527-2 Elongation at break (tensile test) 1.5 % 50 mm/min DIN EN ISO 527-2 Flexural strength 13,200 psi 2 mm/min DIN EN ISO 178 Modulus of elasticity (flexural test) 696,000 psi 2 mm/min DIN EN ISO 178...
Modulus. of elasticity in tension at 23ºC53457N/mm2400-800350-700500-550650500-12002000 Mechanical Maximum bending stress at 23ºC53452Mpa18-20131525-3050 Flexural Modulus53457N/mm2600-800660-680600-650650-7001000-15001950 Ball Hardness 132/6053456N/mm225-3023-29n.kn.25-3034-40120 Rockwell ...
ISO 527-2%彈性模數─拉力試驗後Modulus of elasticity after tensile test ISO 527-2MPa 彈性模數─彎曲試驗後Modulus of elasticity after flexural test ISO 178MPa 硬度─ 洛氏Hardness - Rockwell ISO 2039-2硬度─ 薛氏D Hardness - Shore D DIN 53505 衝擊強度Charpy impact strength at 23℃ISO 179 kJ/...
The abras ion res istance of PTFE /GF increases 2. 83 times and the modulus of elasticity in compression in creases 1. 8 times after irrad iating by 300 kGy electron beam. The increase in crystallinity, wh ich is caused by electron beam irrad ia tion, leads to the improvement on ...