2024 aluminum alloy was implanted with nitrogen then titanium at different titanium target sputtering currents by plasma-based ion implantation(PBII). The appearances were observed by atomic force microscope, and the surface hardness was measured with Knoop hardness tester and the mechanical property ...
The refilled friction stir spot welding experiments of 2024 aluminum alloy were carried out by selecting the stirring head with different materials, and the effect of different process parameters on the morphology and microstructure of the joints was investigated. The results show that H13 steel stirri...
Berezin, Influence of Combined Loading on Microstructure and Properties of Aluminum Alloy 2024-T3, Mater. Eng. Perform., 2013, 22(7), p 3421-3429. doi:10.1007/s11665- 013-0630-zE. Zasimchuk, L. Markashova, O. Baskova, T. Turchak, N. Chausov, V. Hutsaylyuk, and V. Berezin, ...
Properties of Aluminum Alloys 2024 pdf epub mobi 电子书 图书描述 A compilation of data collected and maintained for many years as the property of a large aluminum company, which decided in 1997 to make it available to other engineers and materials specialists. In tabular form, presents data on...
Processing and mechanical properties of 2024 aluminum matrix composites containing Tungsten and
Tribological properties of 2024 aluminum alloy plasma-based ion implanted with nitrogen then titanium doi:CNKI:SUN:ZYSY.0.2003-06-011CNKI中国有色金属学报(英文版)
By employing the orthogonal and ageing-temperature tests, the influences of heat treatment on mechanical properties of 2024 Aluminum alloy sheet were analyzed. The results show that the optimum parameters of 2024 alloy after T62 treatment are in following: solution temperature 498℃, solution time 30...
Aluminum alloy 2024-T3 is an important engineering material which has been widely used in aerospace applications. Under excessive strains, damage will occur and thus mechanical properties of the alloy will be degraded. The degradation of mechanical properties due to excessive strains is referred to as...
1.SchoolofMaterialsScienceandEngineering,NanchangUniversity,Nanchang330031,; 2.SchoolofMechanicalandElectronicEngineering,NanchangUniversity,Nanchang330031, Received20July2007;accepted17October2007 :Themicrostructurecharacteristicsandmechanicalpropertiesof2024wroughtaluminumalloyproducedbyanew rheoformingtechniqueunderas-castan...
Therefore, the current work is focused to study the role of the shape of the new interface in properties of the joints and to control the morphology of intermetallics subsequently. FSW experiments were carried out between aluminum AA2024 and pure copper for different tool offset positions (on ...