Facile preparation of Fe3O4 nanopartieles with cetyltrimethylammonium bromide (CTAB) assistant and a study of its adsorption capacity. Wang Y Q,Cheng R M,Wen Z, et al. Chemical Engineering Journal . 2012Wang Y, Cheng R, Wen Z, Zhao L (2012) Facile preparation of Fe3O4 nanoparticles ...
The Fe 3O 4–chitosan nanoparticles with core-shell structure have been prepared by crosslinking method. Oleic acid modified Fe 3O 4 nanoparticles were firstly prepared by co-precipitation then chitosan was added to coat on the surface of the Fe 3O 4 nanoparticles by physical absorption. The ...
摘要: This review focuses on the preparation of superparamagnetic Fe3O4@SiO2 nanoparticles and its application in catalyst separation.A desired synthesis route can be summarized by comparing the effect of different preparation methods on the morphology and properties of the formed samples....
Growth − dissolution − regrowth transitions of Fe3O4 nanoparticles as building blocks for 3D magnetic nanoparticle clusters under hydrothermal conditions. Langmuir. 2013;29(49):15433. CAS Google Scholar Waldron RD. Infrared spectra of ferrites. Phys Rev. 1955;99(3):1727. CAS Google ...
氨基化磁性纳米粒子的制备及其对pb2 吸附性能研究 preparation of amination magnetic nanoparticles and their application in pb2 adsorption property 热度: 相关推荐 Research Article The Preparation of Glucan-Fe 3 O 4 Magnetic Nanoparticles and Its In Vivo Distribution in Mice Fengdan Jin Key Laboratory...
Fig. 2a indicates that the Fe3O4 particles have an average size of about 265 nm. Fig. 2b is a magnified image of the Fe3O4 nanoparticles, which clearly shows that the nanoparticles were the aggregate from the primary magnetite nanocrystals. Fig. 2c and d clearly demonstrate a clear core...
Preparation and Characterization of Fe3O4 Single Crystal Nanoparticles with High Crystallinity 来自 掌桥科研 喜欢 0 阅读量: 41 作者:J Wang,J Liu,M Lu,M Jian 摘要: FeOsingle crystal nanoparticles were prepared in zero field and in a magnetic field. FeOwith well crystallinity is achieved in a...
在癌细胞内达到一定的浓度范围 该研究为利用Fe 3 O 4 纳米粒子的磁过热疗法治疗肿瘤提供 了细胞层次的实验和理论基础 关键词:Fe 3 O 4 ;纳米粒子;癌细胞 中图分类号:@26文献标识码:A文章编号:1001 0505(2003)02-0205-03 Preparationofmagnetitenanoparticlesandinteractionwithcancercells MaMingZhuYiZhangYuZhang...
Novel core–shell Fe3O4@poly(dopamine) magnetic nanoparticles were prepared through anin situself-polymerization method. The hybrid nanomaterial showed an average core diameter of 11 ± 3 nm and a polymer thin film thickness of 1.8 ± 0.2 nm. The core–shell nanoparticles were employed as solid...
NanoparticlesExpanded graphiteSolution-free routeEnergy storage and conversionA novel Fe3O4-NPs/EG composite was prepared by a facile solution-free route.The solution-free strategy was effective to avoid restacks of the nanosheets of EG.Fe3O4-NPs with dimension <5nm were homogeneously anchored on...