Continuous Use Temp. (UL Yellow Card) (DSC): 50°C Recommended printing conditions: Nozzle Temperature: 200 - 250°C Print Bed Temperature: >60°C Fan Speed 0 - 50% Surface Adhesion Kapton, BigRep SWITCHPLATE Support Breakaway Specifications Safety Sheet BUY BIGREP PETG More Products Dis...
I have a Prusa PETG which includes a notation on the reel: bed temp needs to be between 60-80.Is this special PETG? How do I change the bed temp? Do I need to?It may be important to note that it states "Filament made for Prusa Research." So perhaps this PETG isn't like Prusa...
Easy to print Hard to break 3D PRINTING FILAMENT PLA+ Density(g/cm3) 1.23 Heat Distortion Temp(ºC,0.45MPa) 53 5/10 Melt Flow Index(g/10min) 5.7(190ºC/2.16kg) Tensile Strength(MPa) 61.34 7/10 Elongation at Break(%...
try 235 nozzle, 70-90 bed (higher temp gives better bed adhesion) and fan 30% those are the most important settings, you could play with retraction distance (2-7mm) and speed (25-50mm/s) the petg i use is Verbatim black and even at 180C it stil prints but looses it's gloss and...
Heat Distortion Temp(ºC,0.45MPa) 53 5/10 Melt Flow Index(g/10min) 5.7(190ºC/2.16kg) Tensile Strength(MPa) 61.34 7/10 Elongation at Break(%) 29.92 3/10 Flexural Strength(MPa) 100.27 10/10 Flexural Modulus(MPa) 3824 7/10 IZOD Impact Strength(kJ/M...
PLA Meta filament Print nozzle temperature 185-195℃, Hot bed temp: 50°C-65°C, Print speed: 50-100mm/s, low printing temperature printing for greater energy efficiency.【Glossy Surface & Good Adhesion】Brightly coloured PLA Meta 3d printer filaments bring glossy surface prints to arts, ...
2. 【Great Easy to Print】Feed smoothly and constantly without clogging the nozzle or extrude.Smooth JAYO1.75mm SILK PLA 3D filament(Tolerance Level : ± 0.02mm). 3. 【Recommend Settings】Recommended JAYO SILK filament Print nozzle temperature 205-215℃, Hot bed temp: 60°C-80°C, Print sp...
A higher print speed reduces the volume of the extruded material and decreases the printing quality, in addition to causing defects. In this context, the mechanical strength of the stacked macromolecule chain decreases with increasing printing speed. On the other hand, when the printing speed is ...