You can also try increasing the cooling fan speed to cool the PETG after it leaves the nozzle. Increase Wipe Distance Another important slicer setting that can be tweaked to prevent PETG stringing is the wipe distance. In Cura, this can be adjusted via the Outer Wall Wipe Distance parameter....
Cooling too quickly increases this shrinkage and thus warpage. The easiest way to solve this problem is to turn off the cooling for the first few layers - either completely or adjust fan speed according to printing progress. This ensures that the fan does not directly affect the first layers,...
Print speed: 30 -120mm/s Cooling fan: 0 -20% X -Y Tensile strength: 48.48±0.61MPa Z-axis Tensile strength: 30.48±0.47MPa X -Y Bending modulus: 3531.71±75.79MPa Heat deformation temperature: 97℃ (0.45MPa) Packaging and delivery Selling Units: Single item Single package size: 25X25X8...
Problem: Weak layer adhesion results in layers separating or delaminating during or after printing. Solution: Increase the nozzle temperature to ensure better inter-layer bonding. Slowing down print speed can also improve layer adhesion. Make sure the cooling fan is not set too high, as excessive ...
I usually print PET at: nozzle 215...225°C, bed 90°C, speed 25...30mm/s, layers 0.06...0.20mm thick, and no cooling if there are no overhangs and bridges. If bridges/overhangs, then a little bit of fan is needed, but that reduces layer bonding. And yes, expect more stringing...
Suggested print speed: 35 – 100 mm/s Cooling Fan: yes Suggested heated bed temperature: 50°C – 60°C Build platform: I-BEAM PETG CARBON requires a heated bed in most instances, from 60-80C. We recommend printing on BuildTak, PEI, or using Glue on Glass. If printing on a...
Print Speed < 200 mm/s < 250 mm/s Toughness (Impact Strength - XY) 41.2 kJ/m² 23.2 kJ/m² Strength (Bending Strength - XY) 83 MPa 96 MPa Stiffness (Bending Modulus - XY) 2890 MPa 3700 MPa Layer Adhesion (Impact Strength - Z) 10.7 kJ/m² 7.8 kJ/m² Heat Resistant(HDT...
Print Speed<250 mm/s<200 mm/s Toughness (Impact Strength - XY)23.2 kJ/m²41.2 kJ/m² Strength (Bending Strength - XY)89 MPa70 MPa Stiffness (Bending Modulus - XY)3950 MPa2910 MPa Layer Adhesion (Impact Strength - Z)7.8 kJ/m²10.7 kJ/m² ...
The deformation rate was 100 times larger than in our previous study on R-PETG (where the cross-head speed was 1 mm/min and tensile testing was performed at room temperature). In addition, the testing temperature was about 30 degrees lower, in the present case [14]. For this reason, th...
The machine has the following features: 100 kN (22,500 lbf) capacity; maximum speed 508 mm/min (20 in/min); 1430 mm (56.3 in) vertical test space; and ±0.5% of reading down to 1/200 of load cell capacity and ±1% of reading from 1/200 to 1/500 of the load cell capacity. ...