密度(Density) of melt 1360 kg/m³ - 熔体热导率(Thermal conductivity of melt) 0.3 W/(m K) - 规格的热容融化(Spec. heat capacity of melt) 1870 J/(kg K) - Eff. thermal diffusivity 1.18E-7 m²/s -Diagrams . [/td][/tr][/table] 关键词: DSM PA6-GF50 Akulon® Ultraflow K-...
DensityASTM D792g/cm³ Shrinkage Flow 3.2mmASTM D955in/in Water Absorption 24hrASTM D570% HardnessStandardValueUnit Rockwell Hardness R(Scale)ASTM D785 Mechanical behaviorStandardDryWetUnit Tensile Strength BreakASTM D638psi Elongation BreakASTM D638% ...
to ISO 62 密度(Density) 1550 kg/m³ ISO 1183CharacteristicsProcessingInjection MoldingSpecial CharacteristicsU.V. stabilized or stable to weather, Heat stabilized or stable to heatRegional AvailabilityEurope, Near East/AfricaDisclaimerCopyright M-Base . 关键词: SABIC_IP PA6-GF50 Staramide BG10HU...
(ISO 1043) • PA6-GF50 Physical Dry Conditioned Unit Test Method g/cm³ Density 1.55 -- ISO 1183/A cm³/g Viscosity Number 145 -- ISO 307 Mechanical Dry Conditioned Unit Test Method Tensile Modulus 2.32E+6 1.38E+6 psi ISO 527-2/1A/1 (16000) (9500) (MPa) 30500 18900 psi ...
吸水率(平衡,23℃,50% RH) Water Absorption%ISO 62 吸水率(饱和,23℃) Water Absorption%ISO 62 密度 Densityg/cm³ISO 1183 收缩率(MD) Shrinkage%ISO 294-4 收缩率(TD) Shrinkage%ISO 294-4 机械性能 MECHANICALPLASTRON™ PA6-GF50-01Akulon® Ultraflow K-FHG0单位 ...
Densityg/cm³ASTM D792 收缩率(MD:3.2 mm) Shrinkage%ASTM D955 冲击性能 IMPACTHiFill FR® PA6/6 GF50 FR-N BKHiFill FR® PA6/6 GF50 FR BK单位 UNIT测试方法 TEST METHOD 悬臂梁缺口冲击强度(23℃,3.2mm) Izod Notched Impact strengthJ/mASTM D256 ...
-GF50-01 包装 原产原包 关键词 泰科纳 PA6, PA6-GF50-01, 含50%长玻璃纤维增强,pa6尼龙6树脂 所在地 东莞常平麦元村物流大道西段美吉特一期5栋20号 联系电话 0769-87187279 手机 13711820929 经理 马益群请说明来自顺企网,优惠更多 请卖家联系我 ...
Melt Flow RateISO1133270ºC, 2.16Kgg/10min50 RELATIVE VISCOSITYIS0307 IN 96%H2SO42.47 Specific GravityISO118323ºCg/cm31.13 AshISO3451800ºC,30min%- Mechanical Tensile StrengthISO52750mm/minMPa70 Elongation at BreakISO52750mm/min%100 ...
Density 1.36 g/cm³ ISO 1183 Mechanical Nominal Value Unit Test Method Tensile Modulus 9510 MPa ISO 527-2/1A Tensile Stress (Break) 155 MPa ISO 527-2/1A/5 Tensile Strain (Break) 1.8 % ISO 527-2/1A/5 Flexural Modulus (23°C) 8830 MPa ISO 178 Flexural Stress 250 MPa ISO 178 Impac...
Low water absorption, low density Polyamide 6 (reinforced) UBE NYLON 1015GC3 PA6, M, 14-060, GF15 Reinforced with glass fiber 15%, natural color 1015GC6 PA6, M, 14-100, GF30 Reinforced with glass fiber 30%, natural color 1015GC9 PA6, M, 14-140, GF45 Reinforced with glass fiber 45...