Molten salt corrosion of SiC and Si3N4ceramics. Tressler R E,et al. Journal of the American Ceramic Society . 2006R.E. Tressler et al., "Molten Salt Corrosion of SiC and Si3N4 Ceramics," J. Am. Ceram. Soc., 59, 278-279 (1976)....
熔盐热析出反应金属化si3n4与si3n4的连接 joining of molten salt reaction metallized si3n4 to si3n4,熔盐热析出反应金属化si3n4与si3n4的连接 joining of molten sa..
Kitaoka, and H. Kawamoto, Hot Corrosion of Chemical Vapour Deposited SiC and Si 3 N 4 in Molten Na 2 SO 4 Salt, J. Mater. Sci. , 1998, 33 , p 1031–1036D.-Y. Song,S. Kitaoka,H. Kawamoto.  Hot corrosion of chemical vapour deposited SiC and Si3N4 in molten Na2SO4 salt...
Titanium metallization of Si3N4 ceramics by molten salt reaction: coating microstructure and brazing property. Thin Solid Fims, v. 442, p. 126-129, 2002.WEI, P., LI, J., CHEN, J., Titanium metallization of Si3N4 ceramics by molten salt reaction: coating microstructure and brazing property...
Chen, Titanium metallization of Si3N4 ceramics by molten salt reaction: coating microstructure and brazing property, Thin Solid Films 422 (2002) 126-129.WEI P, LI J, CHEN J. Titanium metallization of Si3N4 ceramics by molten salt reaction: Coating microstructure and brazing property [J]. ...
molten salt reactionsEffects of reaction time, temperature and the initial concentration of potassium fluorotitanate on the deposition of titanium onto Si3N4 ceramics by molten salt reactions have been studied. The composition of the coating layer deposited under different experimental conditions was ...
Using Fe micro powder as catalyst, the α-Si3N4 powder was prepared by molten salt catalytic nitridation in the NaCl-NaF molten salt media. Effects of nitridation temperatures on nitridation of Si powder were investigated. Moreover, composition and microstructure of samples were characterized by ...
Combustion synthesis (CS) of silicon nitride (Si3N4), assisted by molten salt additives under high N-2 pressure, is reported. The effect of salt additives (NaCl, MgCl2, and MgCl2 center dot 6H(2)O) on the reaction temperature and the final alpha-Si3N4 content is studied. The maximum ...
Although silicon nitride is generally considered to be corrosion resistant, relatively little effort has been expended to document in detail the effects of molten salt exposure on the mechanical behavior of silicon nitride ceramics. There have been several studies of the effects of oxidation in ...
Combustion synthesis (CS) of silicon nitride (Si3N4), assisted by molten salt additives under high N2 pressure, is reported. The effect of salt additives (NaCl, MgCl2, and MgCl26H2O) on the reaction temperature and the final 伪-Si3N4 content is studied. The maximum reaction temperature (...