Journal of Materials ScienceX. Cao,B. Rivaux,M. Jahazi,J. Cuddy,A. Birur.Effect of pre- and post-weld heat treatment on metallurgical and tensile properties of Inconel 718 alloy butt joints welded using 4?kW Nd:
The type and amount of fluxes are vital to pellet quality, because they influence the bonding phases formed during pellet induration and their stability during reduction. Figure 15.21 shows the effect of pellet basicity on the compressive strength of fired pellets produced from 100% specularite ...
This paper addresses the microstructure properties relationship of wide gap brazed Inconel 738LC. Amdry 718 and a Ni-Cr-Fe-Si-B alloy were used as high melting particles (HMPs) and low melting particles (LMPs), respectively. The effect of the amount of LMPs, 30, 40, and 50 pct, on...
Effects of scratch tests on the adhesive and cohesive properties of borided Inconel 718 superalloy I. Campos-Silva, A.D. Contla-Pacheco, A. Ruiz-Rios, J. Martínez-Trinidad, ... W.D. Wong-Angel 15 September 2018 Pages 917-927
Effect of pre-recovery solid solution treatment on microstructure and comprehensive properties of Al-11.0Zn-3.0Mg-1.0Cu-0.2Zr-0.16Ti-0.15Er-0.15La alloy Guocheng Xu, Yuntian Luo, Qingshan Zhou, Guoning Bao & Xiaojing Xu Pages: 444-465 Published online: 19 Jun 2024 AbstractforEffect of pre-...
Vacuum TLP bonding of Inconel 617 superalloy using Ni-Cr-Si-Fe-B filler metal: Metallurgical structure and mechanical propertiesEsmaeiliH.MirsalehiS.E.FarzadiA.VACUUM -LONDON THEN OXFORD- PERGAMON-
Most of the test data reported herein were obtained on the alloy given the double aging treatment. The data reported include the results of tensile, impact, rupture, time—deformation, creep, and structural-stability tests.Howard C. Cross
A sequential coupled thermo-mechanical model was developed for laser-based direct energy deposition of single- IN718 and multi-material IN718-Ti6Al4V systems to monitor the thermal stability, solidification characteristics and origin of the residual stresses in each successively deposited layer in real...
The microstructures of an electron beam melted (EBM) nickel-based superalloy (Alloy 718) were comprehensively investigated in as-built and post-treated conditions, with particular focus individually on the contour (outer periphery) and hatch (core) regions of the build. The hatch region exhibited ...
In the present paper, vacuum transient liquid phase bonding of Inconel 617 alloy was studied. The experiments were carried out at 1135 °C for two different holding times of 45 and 300 min, and using Ni-Cr-Si-Fe-B filler metals with 50 and 100 μm thicknesses. The microstructure...