Tensile Strength, Yield 310 MPa 45000 psi Elongation at Break (in 50 mm) 16.0 % 16.0 % Reduction of Area 40.0 % 40.0 % Modulus of Elasticity (Typical for steel) 200 GPa 29000 ksi Bulk Modulus (Typical for steel) 140 GPa 20300 ksi Poissons Ratio (Typical For Steel) 0.290 0.290 Shear ...
J. Maiden, “The effect of impact loading on the static yield strength of a medium-carbon steel,” J. Mech. and Phys. Solids, 6, No. 1, 53–62 (1957).Campbell, J. D., Maiden, G. J. (1957) The effect of impact loading on the static yield strength of a medium-carbon steel....
4: 1045 steel mechanical properties The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered...
The effects of quenching temperature and tempering temperature on the ratio of yield strength to tensile strength (yield ratio) in a medium carbon Cr-Ni-Mo ultra high strength steel have been investigated. After quenching and tempering at 200℃, the yield ratio first decreases and then increases...
Hot forged plates of two microalloyed grades of 1541 steel have been produced by thermomechanical (TMP) forging schedules. The yield strength and Charpy impact toughness are both increased by TMP treatment, compared to a conventional forging schedule. The strength increase is due to reductions in ...
The results suggest that Ti-Mo-bearing medium-carbon steel yield finer microstructure and nano-precipitates during austenite to bainite transformation during both ultrafast cooling and accelerated cooling processes. Yield strength and tensile strength obtained by ultrafast cooling process were higher than ...
Effect of Rolling and Coiling Temperatures on Microstructure and Mechanical Properties of Medium-Carbon Pipeline SteelOCTGMedium-carbon steelCoiling temperatureFinishing mill temperatureMicrostructureOil country tubular goods (OCTG) steels with a low yield ratio (yield strength/tensile strength) and excellent ...
In general, the final microstructures on the centerline consisted of different bainitic features with yield strengths of a ~700 MPa and ~1200 MPa for QST 560 °C and 420 °C, respectively. To determine the factors affecting bendability, as determined by three-point brake press bending tests, ...
Experimental/ carbon steelcoolingforginggrain sizeVickers hardnessyield strength/ forgingcooling ratemicrostructure variablesmedium carbon microalloy forging steelroom temperature tensile strengthNo Abstract available for this article.doi:10.1007/s10853-005-4239-ySüleyman Gndz...
carbon steel to suit a particular design purpose. Tensile specimens were produced from medium carbon steel and were subjected to various forms of heat treatment processes like annealing, normalizing, hardening and tempering. The stiffness, ductility, ultimate tensile strength, yield strength and hardness...