Magnetic alloys consisting of 68.0˜73.0 weight % manganese, (1/10 Mn - 6.6)˜(1/3 Mn - 22.2) weight % carbon, the balance aluminum, which show wasp-waisted magnetic hysteresis loops with the ratio of the residual magnetization 4&pgr;I.sub.r to the intensity of magnetization 4&...
Magnetic hysteresis loops of Co (a) NW and (b) NT arrays in nanoporous alumina templates with center-to-center distances of 105 nm and different outer diameters, measured with the magnetic field applied parallel to the NW/NT long axis. Tables in the insets present the values of coercivity ...
Magnetic hysteresis loops (M−H curve) were measured for the FeGa/Kapton samples with application of in-plane magnetic field using AGFM. The samples were saturated at a field of 1 T prior to each measurement. The magnetic hysteresis curves for FeGa thicknesses of 28 nm and 20 nm are sh...
HYSTERESIS LOOPS OF MAGNETIC BUBBLE MATERIALS AND THE REMANENCE OF BUBBLE LATTICE DOMAIN磁泡材料的磁滞迴线和泡阵磁畴的剩磁气泡动力学非线性振动无粘势流三维Cavitation phenomena and underwater noise mechanism are closely related to bubble dynamics. Under the assumption of inviscid potential flow, a ...
The samples were cooled in an applied field μ0H=0.5 T showing the magnetic hysteresis loops for temperatures near 125 K. a Magnetization as a function of applied magnetic field. The square shape of the loop at 100 K gradually changes to a bipartite transition. b Rxy as a function...
In case of no exchange bias, or weak bias and partial separation of magnetic hysteresis loops of the top and bottom layers, direct measurements of magnetization give us just general information about magnetization reversal in the entire sample, without any respect to the layer, where this reversal...
Obvious unsymmetry magnetic hysteresis loops were observed, in which the magnetization measured in the second(negative) magnetic field route was larger than that measured in the first(positive) one. Meanwhile, the unsymmetry of the hysteresis loops was C doping levels, magnetic fields and ...
The hysteresis loops and susceptibility of a ferromagnetic or ferrimagnetic bilayer system consisting of two magnetic monolayers (A and B) with different spins (SA = 1/2 and SB = 3/2) in the presence of the crystal field in the monolayer B have been studied. Within the effective-field the...
These parameters are then used to calculate the hysteresis losses for the modeled hysteresis. The asymmetric hysteresis loops are also investigated. Findings – The classical GAs are good optimization methods when a pre-defined possible set of solutions is known. If no assumption on solutions is ...
c, d Magnetic hysteresis loops of CFO nanosheet samples measured at different temperatures under out-of-plane (OOP) and in-plane (IP) magnetic field, respectively. e, f Temperature dependence of magnetic susceptibility (M, left axis, solid curves, measured with a field of 0.1 T) and ...