Our composite cathode inks are excellent for fabricating your own SOFC with a composite cathode. The composite cathode inks have demonstrated better adhesion to the dense electrolyte surface which can enhance your overall cell performance. This ink is fabricated using our quality ink manufacturing proces...
Our LSCF-GDC cathode material can be applied by screen printing, painting or spraying after it is formulated into appropriate inks or suspensions. A Quick PSA on PSD Since our LSCF-GDC Composite Cathode Powder is a mixed component powder we do not have a particle size specification. T...
gdc浸渍lscf纤维作为固体燃料电池阴极的制备与表征如下: 1.材料准备:首先需要准备GDC(石榴石型铁酸盐)浸渍液和LSCF(低温烧结铁酸盐)纤维。GDC浸渍液可以通过将GDC粉末溶于适量的溶剂中制备得到。LSCF纤维则需要通过将LSCF粉末按照一定的工艺条件进行烧结制备得到。 2.纤维浸渍:将LSCF纤维放入GDC浸渍液中,进行浸渍处理。
Cu/LSCF > Ag/LSCF > Pt/LSCF > LSCF 而反觀以GDC為主的觸媒在此溫度範圍其對於二氧化碳的催化活性相較於以LSCF為主的觸媒相對低了許多,然而以不同重量比例的LSCF及GDC混合後,發現以100LSCF-50GDC的比例混合對於二氧化碳的催化有較佳的表現,此外本實驗也作了一氧化碳程溫還原實驗(CO-TPR),發現相較於氫氣程...
Liu, Y., et al., A stability study of impregnated LSCF-GDC composite cathodes of solid oxide fuel cells. Journal of Alloys and Compounds, 2013. 578(0): p. 37-43.A stability study of impregnated LSCF-GDC composite cathodes of solid oxide fuel cells.. Yihui Liu,Fangzhong Wang,Bo Chi,...
A位非化学计量对LSCF-GDC复合阴极结构及导电性能的影响 来自 掌桥科研 喜欢 0 阅读量: 222 作者: 张冠铭 摘要: 固体氧化物燃料电池(Solid Oxide Fuel Cell,SOFC)的极化损失主要发生在阴极反应过程,因此SOFC的性能很大程度上取决于阴极材料性质的优劣。钴基钙钛矿材料作为中温固体氧化物燃料电池(IT-SOFC)中最有...
GDC浸渍LSCF纤维作为固体燃料电池阴极的制备与表征.pdf,人工晶体学报 第44 卷第6 期 Vo l. 44 No.6 2015 年6 月 JOURNAL OF SYNTHETIC CRYSTAIβ June ,20l 5 GDC 浸渍 LSCF 纤维作为固体燃料电池 阴极的制备与表征 王岸杰,罗凌虹,程亮,石纪军,曹希文 (景德镇陶瓷学院
Journal of Materials Science Materials in ElectronicsJamale, A. P., Bhosale, C. H., & Jadhav, L. D. (2016). Fabrication and characterization of La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF)-Ce0.9Gd0.1O1.95 (GDC) composite thick film for anode supported solid oxide fuel cells. Journal of Materials...
GDC粉体的粒径对电解质的烧结致密度具有直接的影响,本文分别采用两种不同颗粒尺寸的GDC粉体(D5 0=9.0μm,深圳某公司;D50=32.0μm,宁波SOFCMAN)制备电解质,研究了电解质的烧结性能。研究结果表明,D50=9.0μm的GDC粉颗粒不均匀,有团聚体,经1000℃预烧,然后造粒、压片,1400℃保温4h烧结,获得GDC电解质的吸水...
4.1 GDC粉体的预处理 4.2 GDC电解质片的制备 4.3 预烧温度对深圳 GDC粉体烧结性能的影响 4.4 烧结温度对 2种 GDC粉体性能的影响 4.5 两种不同形貌 GDC粉体的粒度分布 4.6 两种不同形貌 GDC粉体的 XRD 4.7 本章小结 5 微波辅助溶胶凝胶法合成 LSCF粉体 ...