Category HC90 HC92 HC95 HCT95 HC99 HC-ZTA ZrO2 Al2O3 ≥90% ≥92% ≥95% ≥ 95% ≥ 99% ≥75% / ZrO2 / / / / / ≥21% ≥95% Density >3.50g/ cm3 >3.60g/cm3 >3.65g/cm3 >3.70g/cm3 >3.83g/cm3 >4.10g/cm3 >5.90g/cm3 HV 20 ≥900 ≥950 ≥1000...
China Factory White Ceramic Lining Tiles For Cyclone Product Introduction : Customized size support Specification : Category HC90 HC92 HC95 HCT95 HC99 HC-ZTA ZrO2 Al2O3 ≥90% ≥92% ≥95% ≥ 95% ≥ 99% ≥75% / ZrO2 / / / / / ≥21% ≥95% Density >3.50g/ cm3...
The company specializes in the production of HC series wear-resistant ceramic liners(alumina ball, zirconium silicate ball, zirconia toughed alumina ball, zirconium ball), agate ball, polyurethane ball, 92/T95/ZTA wear-resistant ceramic liner (alumina liner, zirconium toughed aluminum comp...
3-2.We do quenching & tempering treatment for high Cr white iron plates to achieve high hardness. 3-3. Cr15Mo3 castings: more than HRC56; AS2027 Cr27 castings: more than HRC59. 4.Chemical Composition: Reference Standard(ISO 21988-2005) Nominal Chemi...
Kaulbach HC, White MV, Igarashi Y, et al: Estimation of nasal epithelial lining fluid using urea as a marker. J Allergy Clin Immunol 92: 457-465, 1993.Kaulbach HC, White MV, Igarashi Y, Hahn BK, Kaliner MA. Estimation of nasal epithelial lining fluid using urea as a marker. J ...
3-2.We do quenching & tempering treatment for high Cr white iron plates to achieve high hardness. 3-3. Cr15Mo3 castings: more than HRC56; AS2027 Cr27 castings: more than HRC59. 4.Chemical Composition: Reference Standard(ISO 21988-2005) ...
The company specializes in the production of HC series wear-resistant ceramic liners(alumina ball, zirconium silicate ball, zirconia toughed alumina ball, zirconium ball), agate ball, polyurethane ball, 92/T95/ZTA wear-resistant ceramic liner (alumina liner...
Category HC90 HC92 HC95 HCT95 HC99 HC-ZTA ZrO2 Al2O3 ≥90% ≥92% ≥95% ≥ 95% ≥ 99% ≥75% / ZrO2 / / / / / ≥21% ≥95% Density >3.50g/ cm3 >3.60g/cm3 >3.65g/cm3 >3.70g/cm3 >3.83g/cm3 >4.10g/cm3 >5.90g/cm3 HV 20 ...
3-2.We do quenching & tempering treatment for high Cr white iron plates to achieve high hardness. 3-3. Cr15Mo3 castings: more than HRC56; AS2027 Cr27 castings: more than HRC59. 4.Chemical Composition: Reference Standard(ISO 21988-2005) Nominal Chemical Composition (W%) Eqv. St...