Hydrogen induced cracking (HIC) testing of low alloy steel in sour environment: Impact of time of exposure on the extent of damage[J] . Jean Kittel,Véronique Smanio,Marion Fregonese,Laurence Garnier,Xavier Lefebvre.Corrosion Science . 2009 (4)...
3) hydrogen-induced crack 氢致裂纹 1. The result showed that the gray cast iron is not more sensitive to the hydrogen-induced crack than high-tensile steel. 采用排液测氢法和插销试验法较系统的研究了氢对钢芯石墨化铸铁焊条焊补的灰口铸铁铸件冷裂倾向的作用 ;将试验结果与高强钢综合比较 ,...
1. 氢致裂纹 HIC是什么意思... ... 5. abbr.hydrogen-induced cracking;氢致裂纹6. abbr. hybrid integrated circuits; 混合集成电路 ... danci.911cha.com|基于4个网页 2. 氢诱导破裂 机械类英语词汇及应用_兰姗姗... ... Hydrogen Embrittlement 氢脆Hydrogen-Induced Cracking氢诱导破裂Impact Test 冲击试...
Welding InternationalSilgado J, Lopez ET, Ramirez AJ, Barrada JG (2011) Evaluation of susceptibility of hydrogen-induced cracking in micro-alloyed armour steel welds using a geometry-modified implant test. Weld Int 25(1):8–14 View Article...
This paper presents a simplified procedure to analyse the Hydrogen Induced Cracking (HIC) of structural steels by means of the Small Punch Test (SPT). Two types of notched specimens were used: one with through-thickness lateral notch and another with surface longitudinal notch. The results for ...
Hydrogen stress cracking, often referred to as hydrogen-induced cracking or static fatigue, is characterized by the brittle fracture of a normally ductile alloy under sustained load in the presence of hydrogen. From: Oil and Gas Corrosion Prevention, 2014 ...
3) sulfide stress corrosion cracking 硫化氢应力腐蚀开裂 1. Accordingly, the accident of sulfide stress corrosion cracking (SSCC) should be taken into account. 针对制造过程中由于开孔失误而进行补焊的冷高压分离器在高压、高浓度的H2S环境的使用安全问题,采用了电化学充氢、恒应变和慢拉伸的实验方法,研究...
The hydrogen-induced cracking (HIC) susceptibility of the X80 steel in H 2 S environment and its heated-treatment microstructure was evaluated. The field emission scanning electron microscopy (FE-SEM), high resolution transmission electron microscopy (HR-TEM) and energy dispersive spectroscopy (EDS) ...
The weld metal in the as‐weld condition in hydrogen induced cracking test showed severe cracking and failed rapidly in the stress corrosion cracking test. 展开 关键词: 17-4 precipitation hardening stainless steel double over aging hydrogen induced cracking stress corrosion cracking reversed austenite ...
In the description of the HIC model presented in Section 6.1, extensive evidence has been provided to support a qualitative assessment of Ti-7 as an excellent choice of material for the drip shield with regard to degradation caused by hydrogen-induced cracking. LTCTF test data observed at LLNL...