3.Hastelloy C2000 Chemical Composition Element Cr Mo Fe Co C Ni Mn Si P S Cu Al Hastelloy C2000 22.0-24.0 15.0-17.0 ≦3.0 ≦2.0 ≦0.01 Bal ≦0.50 ≦0.08 ≦0.025 ≦0.01 1.3～1.9 ≦0.50 4.Hastelloy C2000 Physical Properties Density [g/cm3] 8.5 Melting point [℃] 1328-1358 5.Hastelloy...
HASTELLOY X alloy - a nickel-chromium-iron-molybdenum alloy - has been developed to combine oxidation resistance, fabricability and high-temperature strength. Hastelloy X is also It has also been found to be resistant in petrochemical applications. The Table Below shows theChemical Compositionof Hast...
The main difference between Nicrofer6616hMo and other earlier developed alloys of similar chemical composition is the low carbon, silicon, iron, and tungsten content. Such a chemical composition enables it to exhibit excellent stability at 650-1040°C, improve resistance to intergranular corrosion, ...
Hastelloy C-276相近牌号:W.Nr.2.4819 NiMo16Cr15W (德国) NC17D (法国) CHEMICAL COMPOSITION (WEIGHT %) C (%):≤0.010;Si (%):≤0.08;Mn (%): ≤ 1.00;P (%) ≤: 0.040;S (%) ≤: 0.030;Cr (%):14.5 ~ 16.5;Mo (%): 15.0 ~ 17.0;Co (%): ≤ 2.50;V (%): ≤ 0.35;W (%)...
Chemical Processing.Nominal Composition Cr: 22.0 – 24.0 Mo: 15.0 – 17.0 Fe: 3.0 max Co: 2.0 max Cu: 1.3 – 1.9 Ni: balance C: 0.01 max Mn: 0.5 max Al: 0.5 max Si: 0.08 max P: 0.025 max Physical Properties Density: 0.307 lb/in3, (8.5 g/cm3)Modulus of...
C-276N102762.481914.5-16.55715.0-17.0-45Nickel C-22®N060222.460220.0-22.55612.5-14.5-46Nickel Maximum, unless range or minimum is indicated. Values listed are primary elements only and are not complete chemical compositions as listed in specific product type specifications. ...
Hastelloy C-4国家标准 热处理工艺图 Physical properties of Hastelloy C-4:Density 8.64 g/cm3 Melting point 1350-1400 ℃ Hastelloy C-4 (Ni Cr Mo) has excellent thermal stability and resistance at high temperature The stress corrosion cracking and yangizing atmosphere at high temperature have ...
Hastelloy C-22HS of chemical composition (in wt%) of Cr 21.0, Mo 17.0, Fe 2.0, C 0.01, Si 0.08, balance Ni, subjected to surface grinding treatment to produce a gradient structured material is composed of nanolaminated surface layer, followed by deformation twinned layer and finally the ...
Alloy 22Chemical composition: % Ni Cr Mo Fe W Co C Mn Si P S V min balance 20 12.5 2 2.5 max 22.5 14.5 6 3.5 2.5 0.015 0.5 0.08 0.02 0.02 0 Alloy 22 Physical properties Density 8.69 g/cm3 Melting range 1325-1370ºC Features: Hastelloy C-22 is a...
Physical and mechanical properties Density Melting Point Tensile Strength σb/Mpa Yield strength σp/0.2Mpa Elongation δ/% C-276 8.90g/cm3 1325-1370ºC ≥790 ≥356 ≥56 Chemical Composition Ni Cr Mo Fe C Si Co Mn P S W V max max max max max max max C-276 basis...