Type A:High corrosion resistant coating. Type B:Medium corrosion resistant coating. Type C:Low corrosion resistant coating. Note:When not explicitly specified, the default coating type shall be Type A. Parts contracted and Production Part Approval Processed ("PPAPed") before January 1, 2014, that...
请拖动滑块继续阅读 不看了,直接下载 阅读了该文档的用户还阅读了这些文档 8 p. GMW GMW3035-2012 6 p. GMW GMW3417-2011 9 p. GMW GMW6754-2011 4 p. GMW GMW3371-2011 3 p. GMW GMW3347-2011 5 p. GMW GMW3344-2012 10 p. GMW GMW3341-2011 19 p. GMW GMW3083-2012 10 p...
• Type A 10 cycles (类型A: 10 个循环) • Type B 6 cycles (类型B: 6 个循环) • Type C 2 cycles (类型C: 2 个循环) 3.7.7.2 循环测试后,螺纹头部不得有红锈现象出现。 3.7.8 阴极保护. 涂层的阴极保护能力可以依照GMW3286 进行盐雾测试,其中测试样本必须经过刮削直至基体金属显露出来,刮痕...
The Engineering drawing with GMW3359 without any type shall default to GMW3359 Type B. 3.3.1 Type A: High Corrosion Resistant Coating. Mainly to be used in areas with severe high corrosion environment and in areas with high visibility. 3.3.2 Type B: Medium/High Corrosion Resistant Coating. ...
Type B: Medium corrosion resistant coating. Type C: Low corrosion resistant coating. Note: When not explicitly specified, the default coating type shall be Type A. Parts contracted and Production Part Approval Processed (“PPAPed”) before January 1, 2014, that is without the coating Type (A...
GMW3359的工程图没有任何类型是默认与GMW3359 类型B的。3.3.1 类型A：高耐腐蚀涂层。 主要应用于高腐蚀环境的地方或是高能见度的地方。3.3.2 类型B：中/高耐腐蚀涂层。 应用于严重高/中等严重的腐蚀环境中。3.3.3. 类型C：中/低耐腐蚀涂层。对于外部的应用程序，只使用于严重程度偏低的腐蚀环境中。