Chemical Composition of the deposited metal Alloy Nominal Analysis of Welding Electrode Other UNS ASME/AWS Hardness(HRC) Co Cr W C Ni Mo Fe Si Cobalt Base Alloy Bare Welding Electrodes Stellite1 Bal. 32 12 2.45 ≤3 ≤1 ≤3 ≤2 ≤0.5 R30001 (SF)A5.21 ERCoCr-C ...
Chemical Composition (%) Co Cr Mo C Ni Others Hardness Density Melting Range Bal. 26-29 4.5-6.0 0.20-0.35 2.0-3.0 Fe, Si, Mn 27-40 HRC 8.33 g/cm3 1295-1435 ºC Forms & Grades Bare Rod Grade: Co 1, 6, 12, 21, 25, 32, 190 Process: Oxy-acetylen...
Chemical Composition (%) Co Cr W C Ni Mo Others Hardness Density Melting Range Bal. 28-32 11-13 2.0-3.0 <3.0 <1.0 Fe, Si, Mn 50-58 HRC 8.69 g/cm3 1190-1345 ºC Forms & Grades Bare Rod Grade: Co 1, 6, 12, 21, 25, 32, 190 Process: Oxy-acetylene/...
Chemical Composition (%) Co Cr W C Ni Mo Others Hardness Density Melting Range Bal. 28-32 11-13 2.0-3.0 <3.0 <1.0 Fe, Si, Mn 50-58 HRC 8.69 g/cm3 1190-1345 ºC Forms & Grades Bare Rod Grade: Co 1, 6, 12, 21, 25, 32, 190 Process:...