Engineering steel material EN19 hardness in HRC: Flame or induction hardening can give a case hardness of 50 HRC or higher. EN19 equivalent material with AISI 4140, DIN 42CrMo4 EN 1.7225, GB 42CrMo, JIS SCM440C alloy engineering steel Mechanical properties of steel EN19 (1.7225) Rm– Tensile...
elements.Compared with AISI 4130, it has a higher carbon content with good balance of strength, toughness ,abrasion and impact resistance and heat treatment capabilities,but poor in weldability characteristics.AISI 4140 is generally supplied in quenched and tempered ...
SAE 4140 alloy steel is usually supplied ready heat treated to hardness in 18-22 HRC. If further heat treatment is required, then heat to 840 oC - 875 oC, hold until temperature is uniform throughout the section, soak for 10 - 15 minutes per...
SAE 4140 alloy steel is usually supplied ready heat treated to hardness in 18-22 HRC. If further heat treatment is required, then heat to 840 oC - 875 oC, hold until temperature is uniform throughout the section, soak for 10 - 15 minutes per 25 ...
elements.Compared with AISI 4130, it has a higher carbon content with good balance of strength, toughness ,abrasion and impact resistance and heat treatment capabilities,but poor in weldability characteristics.AISI 4140 is generally supplied in quenched and tempered condition ...
SAE 4140 alloy steel is usually supplied ready heat treated to hardness in 18-22 HRC. If further heat treatment is required, then heat to 840 oC - 875 oC, hold until temperature is uniform throughout the section, soak for 10 - 15 minutes per ...